应力发光材料BaZrSi<sub>3</sub>O<sub>9</sub>的制备与发光特性研究

傅胤荣; 胡义华; 金亚洪

doi:10.3969/j.issn.1007-7162.2015.04.003

欢迎来到能源电力期刊网！

English Version 期刊登录

您当前的位置：

首页 >

文章列表页 >

应力发光材料BaZrSi₃O₉的制备与发光特性研究

综合研究 | 更新时间：2026-05-27

- 应力发光材料BaZrSi₃O₉的制备与发光特性研究
- Preparation and Mechanoluminescent properties of BaZrSi₃O₉
- 广东工业大学学报 2015年32卷第4期页码：17-20
- 作者机构：
- 作者简介：
  
  傅胤荣（1979-），男，副教授，博士研究生，主要研究方向为稀土发光材料.胡义华（1958-），男，教授，主要研究方向为稀土发光材料. E-mail: huyh@gdut.edu.cn
- 基金信息：
  
  国家自然科学基金资助项目（21471038）
- DOI：10.3969/j.issn.1007-7162.2015.04.003
  中图分类号：
- 网络首发：2015-12-04，
  
  纸质出版：2015
- 稿件说明：
移动端阅览
傅胤荣, 胡义华, 金亚洪. 应力发光材料BaZrSi₃O₉的制备与发光特性研究[J]. 广东工业大学学报, 2015, 32(4): 17-20. DOI: 10.3969/j.issn.1007-7162.2015.04.003.

Fu Yin-rong, Hu Yi-hua, Jin Ya-hong. Preparation and Mechanoluminescent properties of BaZrSi₃O₉[J]. 2015, 32(4): 17-20. DOI: 10.3969/j.issn.1007-7162.2015.04.003.
傅胤荣, 胡义华, 金亚洪. 应力发光材料BaZrSi₃O₉的制备与发光特性研究[J]. 广东工业大学学报, 2015, 32(4): 17-20. DOI: 10.3969/j.issn.1007-7162.2015.04.003. DOI：

Fu Yin-rong, Hu Yi-hua, Jin Ya-hong. Preparation and Mechanoluminescent properties of BaZrSi₃O₉[J]. 2015, 32(4): 17-20. DOI: 10.3969/j.issn.1007-7162.2015.04.003. DOI：

摘要

采用高温固相法制备了BaZrSi

样品，通过X 射线粉末衍射仪、荧光光谱仪和热释光计量计测试了样品的物相结构、荧光光谱、余辉衰减曲线、热释光温度曲线和应力发光特性.测试结果表明：发射光谱峰位于435 nm，具有可重复利用性，属于非破坏性发光，样品应力发光强度与承受的机械应力在一定范围内成正比的规律性.研究表明应力发光的原理与长余辉相似，缺陷势阱捕获的电荷载流子受到外界的影响而释放，与发光中心复合从而产生发光.样品波长属于可见光，可以用作检测应力强度及探测结构破坏位置的图像传感器，从而实现非破坏性应力实时监测及应力可视化.

Abstract

Mechanoluminescence is a type of luminescence caused by the application of mechanical energy to solids. In this paper

powder of BaZrSi

is synthesized by the conventional solid state reaction. Then thermoluminescence and mechanoluminescent properties are studied. Phase and crystal structure of the obtained materials can be determined by X-ray diffraction (XRD). Hence photoluminescent spectrum and mechanoluminescent measurement show that the emission peak is about 435 nm. The mechanoluminescence results present that the intensities of samples are well dependent on the stress

indicating that these mechanoluninescent materials can be potentially used as sensors to detect the dynamic visualization of stress distribution of an object. The results also suggest that

the trap and the worse symmetry of crystal structure are responsible for the mechanoluninescent intensity of BaZrSi

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

具守恒量波动方程的循环双子网物理信息神经网络

双模态迭代交叉注意力融合集成框架

基于路况参数的混合动力机车能量管理策略研究

融合沟道倾斜角的3D NAND存储单元建模及编程策略优化

人工噪声辅助无人机太赫兹安全通信的鲁棒设计

应力发光材料BaZrSi3O9的制备与发光特性研究

Preparation and Mechanoluminescent properties of BaZrSi3O9

DOI：10.3969/j.issn.1007-7162.2015.04.003

摘要

Abstract

关键词

Keywords

references

应力发光材料BaZrSi₃O₉的制备与发光特性研究

Preparation and Mechanoluminescent properties of BaZrSi₃O₉