高温水中硫酸根离子质量浓度对Z3CN20.09不锈钢应力腐蚀开裂的影响

张锦浙; 陈红雨; 张裕; 吴迪

doi:10.19666/j.rlfd.202201034

欢迎来到能源电力期刊网！

English Version 读者登录期刊登录

您当前的位置：

首页 >

文章列表页 >

高温水中硫酸根离子质量浓度对Z3CN20.09不锈钢应力腐蚀开裂的影响

发电技术论坛 | 更新时间：2025-09-28

- 高温水中硫酸根离子质量浓度对Z3CN20.09不锈钢应力腐蚀开裂的影响
- Effect of mass concentration of sulfate ions in high temperature water on stress corrosion cracking behavior of Z3CN20.09 stainless steel
- 热力发电 2022年51卷第9期页码：162-169
- 作者机构：
  
  大亚湾核电运营管理有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.202201034
  中图分类号： TM623;TG172.9
- 纸质出版日期：2022
- 稿件说明：
移动端阅览
张锦浙, 陈红雨, 张裕, 等. 高温水中硫酸根离子质量浓度对Z3CN20.09不锈钢应力腐蚀开裂的影响[J]. 热力发电, 2022,51(9):162-169.

ZHANG Jinzhe, CHEN Hongyu, ZHANG Yu, et al. Effect of mass concentration of sulfate ions in high temperature water on stress corrosion cracking behavior of Z3CN20.09 stainless steel[J]. Thermal power generation, 2022, 51(9): 162-169.
张锦浙, 陈红雨, 张裕, 等. 高温水中硫酸根离子质量浓度对Z3CN20.09不锈钢应力腐蚀开裂的影响[J]. 热力发电, 2022,51(9):162-169. DOI： 10.19666/j.rlfd.202201034.

ZHANG Jinzhe, CHEN Hongyu, ZHANG Yu, et al. Effect of mass concentration of sulfate ions in high temperature water on stress corrosion cracking behavior of Z3CN20.09 stainless steel[J]. Thermal power generation, 2022, 51(9): 162-169. DOI： 10.19666/j.rlfd.202201034.

摘要

采用慢应变速率试验(SSRT)测试了模拟压水堆核电厂一回路水中硫酸根离子(SO_4~(2–))质量浓度对Z3CN20.09铸造奥氏体不锈钢(CASS)应力腐蚀开裂(SCC)敏感性的影响。测试结果表明:Z3CN20.09不锈钢在6种水环境中进行SSRT后断口附近都出现不同程度的颈缩现象;在不含SO_4~(2–)的正常压水堆(PWR)水质中

不锈钢的破断延伸率最大

断裂面均为韧窝状的断口

SCC抗力强;高温水中SO_4~(2–)质量浓度为100～1 500μg/L时

SSRT断口出现明显的SCC现象

断口表现为脆性+韧窝混合型;不同相及相界对SO_4~(2–)腐蚀的敏感性和SO_4~(2–)对合金表面钝化膜的劣化作用是促进Z3CN20.09铸造奥氏体不锈钢局部腐蚀和SCC的重要因素。

Abstract

By slow strain rate test(SSRT)

the effect of sulfate mass concentration in primary circuit water of the pressurized water reactor(PWR) on stress corrosion cracking(SCC) sensitivity of Z3CN20.09 casted austenitic stainless steel(CASS) was investigated. The results show that

necking occurred near the fracture after the SSRT of Z3CN20.09 CASS in 6 water environments. In normal PWR water containing no SO_4~(2–)

the elongation to fracture of Z3CN20.09 CASS was the largest

and the rupture surfaces were dimple-like facets

indicating that the Z3CN20.09 CASS has excellent SCC resistance under this condition. SSRT samples showed significant SCC sensitivity in high-temperature water containing 100～1 500 μg/L SO_4~(2–)

and the fracture showed transgranular plus dimple mixed face. The corrosion sensitivity of different phases and phase boundaries to SO_4~(2–) and the deterioration effect of SO_4~(2–) on passive film on the alloy surface are thought to be the key factors for enhancing localized corrosion and SCC.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

燃机进气安全隔离滤网钢丝失效原因分析

恒电位阴极极化法评价阻垢剂性能试验条件的优化

超超临界机组过/再热器氧化皮生长试验研究

130℃热网循环水中316L和317L不锈钢换热板点蚀临界条件实验研究

氯离子质量浓度对Inconel 740H合金应力腐蚀开裂性能的影响