华能福州电厂锅炉水冷壁氢损伤爆管分析

更新时间：2025-09-28

- 华能福州电厂锅炉水冷壁氢损伤爆管分析
- ANALYSIS OF TUBE-BURST DUE TO HYDROGEN DAMAGE OF WATER-WALL IN BOILER OF HUANENG FUZHOU POWER PLANT
- 热力发电 2006年第11期页码：68-71
- 作者机构：
  
  1. 华能福州电厂
  2. 西安热工研究院有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2006.11.025
  中图分类号： TK223.31
- 纸质出版：2006
- 稿件说明：
移动端阅览
黄瑾, 陈吉刚. 华能福州电厂锅炉水冷壁氢损伤爆管分析[J]. 热力发电, 2006,(11):68-71.

HUANG Jin, CHEN Ji-gang. ANALYSIS OF TUBE-BURST DUE TO HYDROGEN DAMAGE OF WATER-WALL IN BOILER OF HUANENG FUZHOU POWER PLANT[J]. Thermal power generation, 2006, (11): 68-71.
黄瑾, 陈吉刚. 华能福州电厂锅炉水冷壁氢损伤爆管分析[J]. 热力发电, 2006,(11):68-71. DOI： 10.19666/j.rlfd.2006.11.025.

HUANG Jin, CHEN Ji-gang. ANALYSIS OF TUBE-BURST DUE TO HYDROGEN DAMAGE OF WATER-WALL IN BOILER OF HUANENG FUZHOU POWER PLANT[J]. Thermal power generation, 2006, (11): 68-71. DOI： 10.19666/j.rlfd.2006.11.025.

摘要

通过对有关管样的试验分析

认为华能福州电厂2号炉水冷壁爆管是一起因柠檬酸酸洗不当引发的氢损伤爆管。分析了由柠檬酸引起的垢下氢腐蚀损伤特征

并通过采用羟基乙酸+甲酸进行再次酸洗

消除了隐患。迄今

2号炉水冷壁管运行正常

没有再发生垢下腐蚀和氢损伤。

Abstract

Directing against the tube-burst failure of water-wall in boiler no.2 of Huaneng Fuzhou Power Plant

through test and analysis of related tube samples

it is believed that the said failure is due to tube-burst of hydrogen damage resulting from unsuitable acid cleaning with citric acid solution.The characteristics of hydrogen corrosion damage under scale caused by citric acid have been analysed

and the said hydrogen damage under scale being preliminarily approached. After adopting hydroxyacetic acid + formic acid to carry out cleaning again

the hidden peril has been removed.So far

the water-wall of boiler no.2 is in normal operation

corrosion and hydrogen demage under scale haven't been discovered again.

关键词

Keywords

references

浏览量

201

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

某DG440/13.7-Ⅱ2型循环流化床锅炉水冷壁爆管原因分析

警惕锅炉酸洗不当引起的爆管事故

对冲燃烧锅炉水冷壁高温腐蚀运行调整

燃煤电站锅炉受热面灰污监测与智能吹灰控制技术

超超临界1 000 MW机组锅炉水冷壁壁温偏差计算分析及对策