- 燃机进气安全隔离滤网钢丝失效原因分析
- CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE
- 热力发电 2004年第12期页码：48-50
- 作者机构：
  
  1. 月亮湾燃机电厂
  2. 华南理工大学,广东,深圳,518052
  3. ,广东,广州,510641
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2004.12.015
  中图分类号： TK47
- 纸质出版：2004
- 稿件说明：
移动端阅览
陈鹏, 甘孟必, 高岩. 燃机进气安全隔离滤网钢丝失效原因分析[J]. 热力发电, 2004,(12):48-50.

CHEN Peng, GAN Meng-bi, GAO Yan et al. CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE[J]. Thermal power generation, 2004, (12): 48-50.
陈鹏, 甘孟必, 高岩. 燃机进气安全隔离滤网钢丝失效原因分析[J]. 热力发电, 2004,(12):48-50. DOI： 10.19666/j.rlfd.2004.12.015.

CHEN Peng, GAN Meng-bi, GAO Yan et al. CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE[J]. Thermal power generation, 2004, (12): 48-50. DOI： 10.19666/j.rlfd.2004.12.015.

摘要

通过对月亮湾燃机电厂 3号燃机进气安全隔离滤网失效的不锈钢钢丝进行无损检测和其化学成分、金相、能谱以及断口分析等

确定不锈钢钢丝合金比例不当、锰含量太高且晶间析出碳化物 ;材质存在严重质量问题。建议钢丝材料选用超低碳、铬镍含量高、含钼 2 %～ 3 %的 0 0Cr1 7Ni1 4Mo3或 3 1 6L( 0 0Cr1 7Ni1 4Mo2 )奥氏体不锈钢

且制造应符合GB 4 2 4 0要求

Abstract

Throung tests of non-destructive detection

analysis of chemical composition

metallurgy

energy spectrum

and fractures for the failed reinforcing wires of incoming gas safety isolating strainer on gas turbine No.3 in Yueliangwan Gas Tubine Power Plant

it is determined that one cause leading to early fracture is unsuitable proportion of alloy composition for the stainless wires

the content of mangonese being high

eduction of intergranular carbide

as well as sirious quality problems existing in the material used. It is recommended to select OOCr 17 Ni14 Mo3 or 316L (OOCr17N:14MoZ) austenitic stainless steel having ultta-low carbon content

high Cr and Ni content

and 2%～3%Mo content

and the fabrication of reinforcing wires having to be in conformity with requirements of standard GB4240.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

18-8型奥氏体不锈钢锅炉管服役特性研究(六)

大型燃气轮机余热锅炉进口烟道速度均匀性研究

降低联合循环机组整体性能试验不确定度的措施

住宅小区天然气热电冷三联产方案及其技术经济性能分析

燃气轮机起动过程研究综述与展望