As one of the perfect geometries in nature

sphere is common in the daily and industrial life. The mechanical properties of sphere are of great significance to engineering safety and numerical simulation. Internal cracks or defects are inherent properties of materials

and have an important influence on the mechanical properties of materials. However

the internal crack of sphere is not considered in the current research due to the limit of technology. Thus

understanding of the propagation of internal cracks of brittle sphere is limited. In our study

internal cracks were created in glass sphere samples by 3D-ILC (3D-internal laser-engraved crack). Uniaxial compression tests were performed on samples with an internal crack at 60°. By comparing with results of samples without a 60° internal crack

the propagation of the internal crack

the load and the fractography were investigated. The distributions of KI

KII

KIII were calculated using M-integral. Results showed that: 1) the fracture patterns include wing cracks and primary crack. 2) Wing crack is composed of smooth zone (mode I-II fracture) and tear zone (mode I-II-III fracture). 3) The distributions of KI

KII

KIII around crack tips obtained by M-integral are consistent with the test results. 4) 3D-ILC can be successfully applied into the investigation of internal cracks of sphere and it provides experimental and theoretical basis for the study of 3D problem

internal cracks and mode I-II-III fracture in fracture mechanics of brittle materials.