- 考虑间歇充填和浓度效应的充填体长期强度试验研究
- Experimental study of long-term mechanical strength of cemented tailings backfill considering effect of filling interval time and solid content
- 岩土力学 2018年39卷第S1期页码：341-347
- 作者机构：
  
  1. 北京科技大学土木与资源工程学院,北京,100083
  2. 北京科技大学金属矿山高效开采与安全教育部重点实验室,北京,100083
- 作者简介：
- 基金信息：
- DOI：10.16285/j.rsm.2017.2311
  中图分类号： TD853
- 网络首发：2018-09-02，
  
  纸质出版：2018
- 稿件说明：
移动端阅览
曹帅, 宋卫东, 薛改利. 考虑间歇充填和浓度效应的充填体长期强度试验研究[J]. 岩土力学, 2018,39(S1):341-347.

CAO Shuai, SONG Wei-dong, XUE Gai-li. Experimental study of long-term mechanical strength of cemented tailings backfill considering effect of filling interval time and solid content[J]. 2018, 39(S1): 341-347.
曹帅, 宋卫东, 薛改利. 考虑间歇充填和浓度效应的充填体长期强度试验研究[J]. 岩土力学, 2018,39(S1):341-347. DOI： 10.16285/j.rsm.2017.2311.

CAO Shuai, SONG Wei-dong, XUE Gai-li. Experimental study of long-term mechanical strength of cemented tailings backfill considering effect of filling interval time and solid content[J]. 2018, 39(S1): 341-347. DOI： 10.16285/j.rsm.2017.2311.

摘要

为探究不同充填间隔时间(FTS)和料浆浓度对胶结充填体长期强度影响机制，配制70%、72%、75%三个浓度、充填间隔时间为12、24、36、48 h的两分层胶结充填体试件，开展单轴抗压强度(UCS)试验并探究其力学特性及其破坏形式。试验结果表明，（1）胶结充填体峰值抗压强度随充填间隔时间增大而呈递减趋势，充填间隔时间一定时胶结充填体抗压强度随料浆浓度增大而增大，且峰值抗压强度与充填间隔时间呈多项式函数规律；（2）胶结充填体试件加载过程中表现为压密阶段、线弹性阶段、裂纹扩展阶段和破坏发展4个阶段，随充填间隔时间延长，胶结充填体的破坏形式可能表现为张拉破坏–拉剪破坏过渡–拉剪混合破坏的损伤模式。研究结论能够为后期充填体强度设计和稳定性控制提供有益参考。

Abstract

In order to investigate the influence mechanism of the long-term strength of cemented tailings backfill(CTB) with different filling interval times(FITs) and solid contents(SDs). The uniaxial compression strength(UCS) test was carried out by using two layered CTB specimens with three SDs of 70%

72% and 75%

four FITs of 12

36 h and 48 h. And the mechanical properties and its failure forms were investigated. The results show that: (1) The peak compressive strength of CTB decreases with the increases of filling interval. When the FIT is fixed

the UCS value increases along with the SD

and the peak compressive strength and filling interval are polynomial. (2) During the loading process

four stages of the compaction

line elastic

crack propagation and failure development are shown. With the extension of interval time

the failure forms of CTB may represent as the tension failure-shear failure transition-shear mixing damage. The conclusion can provide a useful reference for the strength design and stability control of CTB.

关键词

Keywords

references

浏览量

225

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

扩展基础冲剪破坏特征试验研究

双临空面岩质边坡滑动与倾倒破坏的运动学分析

基于巴西劈裂试验的页岩强度与破坏模式研究

多节理岩体裂纹扩展及变形破坏试验研究

不同应力路径条件下原状Q3黄土的强度特性及破坏方式试验研究