气泡混合轻质土干湿循环和硫酸钠耐久性试验研究

基础理论与实验研究 | 更新时间：2026-06-25

- 气泡混合轻质土干湿循环和硫酸钠耐久性试验研究
- A durability experimental study of lightweight soil subjected to wetting-drying cycles and sodium sulfate soaking
- 岩土力学 2015年36卷第S1期页码：362-366
- 作者机构：
  
  1. 东南大学岩土工程研究所,江苏,南京,210096
  2. 东南大学江苏省城市地下工程与环境安全重点实验室,江苏,南京,210096
- 作者简介：
- 基金信息：
  
  国家自然科学基金（No.41472258，No.51278100）;江苏省杰出青年基金（No.BK2012022）
- DOI：10.16285/j.rsm.2015.S1.062
  中图分类号： TU443
- 网络首发：2018-06-14，
  
  纸质出版：2015
- 稿件说明：
移动端阅览
刘楷, 李仁民, 杜延军, 等. 气泡混合轻质土干湿循环和硫酸钠耐久性试验研究[J]. 岩土力学, 2015,36(S1):362-366.

LIU Kai, LI Ren-min, DU Yan-jun, et al. A durability experimental study of lightweight soil subjected to wetting-drying cycles and sodium sulfate soaking[J]. 2015, 36(S1): 362-366.
刘楷, 李仁民, 杜延军, 等. 气泡混合轻质土干湿循环和硫酸钠耐久性试验研究[J]. 岩土力学, 2015,36(S1):362-366. DOI： 10.16285/j.rsm.2015.S1.062.

LIU Kai, LI Ren-min, DU Yan-jun, et al. A durability experimental study of lightweight soil subjected to wetting-drying cycles and sodium sulfate soaking[J]. 2015, 36(S1): 362-366. DOI： 10.16285/j.rsm.2015.S1.062.

摘要

采用水泥和地聚合物作为固化剂制备气泡混合轻质土，测试水泥轻质土（LCSC）和地聚合物轻质土（LGSC）在干湿循环和硫酸钠长期浸泡环境下的无侧限抗压强度和质量变化率，并相互进行对比，分析干湿循环级数和硫酸钠浸泡环境对其强度特性的影响规律。结果表明，标准养护地聚合物轻质土强度约为水泥轻质土的2倍；干湿循环后地聚合物轻质土强度随干湿循环级数衰减较快且破坏程度逐渐增大，水泥轻质土强度未出现明显衰减，与水泥轻质土相比，地聚合物轻质土抗干湿能力较差；硫酸钠溶液浸泡120 d后，地聚合物轻质土强度出现小幅下降，约为标准养护28 d试样的80%；水泥轻质土出现开裂破坏，与水泥轻质土相比，地聚合物轻质土抗硫酸钠侵蚀能力较强。

Abstract

In this study

cement and geopolymer are added to lightweight soil as binders. For the purpose of comparison

unconfined compressive strength test is conducted to evaluate the effects of wetting-drying cycles and sodium sulfate soaking on the strength properties of lightweight cement stabilized clay(LCSC) and lightweight geopolymer stabilized clays(LGSC). The change of unconfined compressive strength and mass loss with wetting-drying cycles and sodium sulfate soaking are discussed. The results show that the values of unconfined compressive strength of LGSC are 2 times that of LCSC under the standard curing condition. Upon wetting-drying cycles

the unconfined compressive strength of LGSC decreases more rapidly than that of LCSC. Compared with LCSC

the wetting-drying durability of LGSC is weaker. After sulfate solution soaking for 120 days

unconfined compressive strength of LGSC declines slightly. However the surface of LCSC cracks. Compared with LCSC

the wetting-drying durability of LGSC is stronger.

关键词

Keywords

references

浏览量

468

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

泥质岩膨胀各向异性与循环胀缩特征

基于饱和指数模型的坝基帷幕体防渗效果及耐久性研究

水泥固化重金属污染土的强度特性试验研究

干旱区土建筑遗址冻融耐久性研究

土建筑遗址干湿耐久性研究