垃圾填埋场污泥灰改性黏土衬垫的强度特性及微观结构

董祎挈; 陆海军; 李继祥; 徐文颖

doi:10.16285/j.rsm.2015.S1.031

欢迎来到能源电力期刊网！

English Version 期刊登录

您当前的位置：

首页 >

文章列表页 >

垃圾填埋场污泥灰改性黏土衬垫的强度特性及微观结构

基础理论与实验研究 | 更新时间：2026-06-25

- 垃圾填埋场污泥灰改性黏土衬垫的强度特性及微观结构
- Strength properties and microstructure of landfill clay liner containing sewage sludge ash
- 岩土力学 2015年36卷第S1期页码：187-192
- 作者机构：
  
  武汉轻工大学多孔介质力学研究所,湖北,武汉,430023
- 作者简介：
- 基金信息：
  
  湖北省教育厅科学研究计划项目（No.D20141703）;湖北省自然科学基金（No.2014CFB889）
- DOI：10.16285/j.rsm.2015.S1.031
  中图分类号： X53
- 网络首发：2018-06-14，
  
  纸质出版：2015
- 稿件说明：
移动端阅览
董祎挈, 陆海军, 李继祥, 等. 垃圾填埋场污泥灰改性黏土衬垫的强度特性及微观结构[J]. 岩土力学, 2015,36(S1):187-192.

DONG Yi-qie, LU Hai-jun, LI Ji-xiang, et al. Strength properties and microstructure of landfill clay liner containing sewage sludge ash[J]. 2015, 36(S1): 187-192.
董祎挈, 陆海军, 李继祥, 等. 垃圾填埋场污泥灰改性黏土衬垫的强度特性及微观结构[J]. 岩土力学, 2015,36(S1):187-192. DOI： 10.16285/j.rsm.2015.S1.031.

DONG Yi-qie, LU Hai-jun, LI Ji-xiang, et al. Strength properties and microstructure of landfill clay liner containing sewage sludge ash[J]. 2015, 36(S1): 187-192. DOI： 10.16285/j.rsm.2015.S1.031.

摘要

为评价污泥灰改性黏土作为填埋场衬垫防渗材料的可行性，分析污泥灰改性黏土强度特性及孔隙结构，针对受垃圾渗沥液腐蚀的纯黏土与污泥灰掺量为1%～5%的改性黏土，采用直接剪切试验分析其抗剪强度变化规律，采用低温氮气吸附试验分析剪切变形后试样的孔隙结构组成。结果表明，改性黏土属于VI型等温线，并存在H3型滞后环，且2～6 nm介孔的数量占比较大。受垃圾渗沥液腐蚀后，黏土抗剪强度大幅下降，黏聚力与内摩擦角分别下降60.12%和19.17%；黏土的最大氮气吸附量降低16.19%，且孔隙分布双肩峰发育不完全；随污泥灰添加量的增加，改性黏土抗剪强度增大，且孔隙分布逐渐恢复双肩峰形式，总孔容增大。

Abstract

In order to evaluate the feasibility of improved clay based on sewage sludge ash(SSA) used as landfill liner-soil materials

a series of the direct shear strength tests and low temperature nitrogen adsorption tests were carried out to analyze shear strength and pore structure of improved clay in laboratory. The improved clay was composed of 95%-99% of raw clay and 1%-5% of SSA. The results show that the isotherms of improved clay containing SSA is belong to type VI isotherms

and it had type H3 hysteresis loop; The pore of improved clay was mainly composed of mesopore of 2-6 nm. The shear strength of raw clay corroded by landfill leachate sharply decreased. The cohesive strength and internal friction angle of sample declined 60.12% and 19.17%

respectively. The maximum adsorption capacity of raw clay corroded by landfill leachate declined 16.19%. The shear strength and pore volume of improved clay increased with an increasing of SSA.

关键词

Keywords

references

浏览量

173

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

富碱性水环境砂质泥岩孔隙结构演化与分形特征研究

复杂岩性储层渗透率-应力敏感性及其对气井产能的影响

液氮冻结条件下岩石孔隙结构损伤试验研究

钙质砂颗粒内孔隙的结构特征分析

不同孔隙类型火山岩储层渗透率应力敏感特征