- 电站锅炉受热面涂层抗高温氧化性能的研究
- STUDY ON HIGH-TEMPERATURE OXIDATION RESISTANT PROPERTY OF COATINGS ON HEATING SURFACE IN UTILITY BOILERS
- 热力发电 2010年39卷第3期页码：53-56
- 作者机构：
  
  1. 沈阳工业大学材料科学与工程学院
  2. 沈阳工程学院动力工程系
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TM621.2
- 纸质出版：2010
- 稿件说明：
移动端阅览
张小辉, 刘正, 王树群. 电站锅炉受热面涂层抗高温氧化性能的研究[J]. 热力发电, 2010,39(3):53-56.

ZHANG Xiao-hui1, LIU Zheng1, WANG Shu-qun21.College of Material Science and Engineering. STUDY ON HIGH-TEMPERATURE OXIDATION RESISTANT PROPERTY OF COATINGS ON HEATING SURFACE IN UTILITY BOILERS[J]. Thermal power generation, 2010, 39(3): 53-56.
张小辉, 刘正, 王树群. 电站锅炉受热面涂层抗高温氧化性能的研究[J]. 热力发电, 2010,39(3):53-56. DOI：

ZHANG Xiao-hui1, LIU Zheng1, WANG Shu-qun21.College of Material Science and Engineering. STUDY ON HIGH-TEMPERATURE OXIDATION RESISTANT PROPERTY OF COATINGS ON HEATING SURFACE IN UTILITY BOILERS[J]. Thermal power generation, 2010, 39(3): 53-56. DOI：

摘要

针对电站锅炉受热面因高温氧化而导致的爆漏

采用Q235低碳钢作为基体

分别喷涂PS45、FeCrAl、4Cr13等3种涂层

与没有涂层保护的钢研102钢管材进行抗高温氧化试验。结果表明

没有涂层保护的钢研102钢抗氧化能力较差

而Q235低碳钢经电弧喷涂保护后其抗氧化性能得到大幅度的提高。其中

PS45涂层中由于Cr、Ni含量较高

在试样表面可持续形成结构致密、性质稳定的Cr2O3保护层

具有优异的抗氧化性能

使试样得到充分保护。

Abstract

Directing against tube-burst and leakage problems of heating surface in utility boilers due to high-temperature oxidation

taking Gangyan 102 steel as the base metal

three kinds of coatings

namely PS45

FeCrAl

and 4Cr13

have been sprayed respectively

a test of high-temperature oxidation resistant coatings on heating surface being carried out.Results show that the oxidation resistant capability of Gangyan 102 boiler tube material proper without coating is worse

after spraying protective coating by using electric arc

the oxidation resistant behavior of 102 steel has been enhanced by a big margin.In three kinds of coatings

owing to Cr and Ni content in PS45 coating is higher

a protective coating of Cr2O3 with compact texture and stable behavior can be continuously formed on surface of the specimen

boasting outstanding oxidation resistant behavior

making the specimen to be fully protected.

关键词

Keywords

references

浏览量

147

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

超超临界1 000 MW机组双切圆锅炉主再热汽温提升方法研究

某新型蒸汽脉冲式声频清灰器清灰机理及经济性分析

锅炉尾部烟道受热面智能燃气吹灰

超(超)临界机组锅炉壁温测点布置优化

DG220/100-4型锅炉主蒸汽温度偏低问题分析与处理