- 某电厂锅炉屏式再热器夹持管爆管原因分析
- CAUSE ANALYSIS OF CONTINUOUS TUBE BURST ON HOLDING PIPES OF THE SCREEN-TYPE REHEATER FOR BOILER NO1 IN ONE POWER PLANT
- 热力发电 2012年41卷第2期页码：88-90
- 作者机构：
  
  甘肃电力科学研究院
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TK228
- 纸质出版：2012
- 稿件说明：
移动端阅览
赵明忠, 吴凯. 某电厂锅炉屏式再热器夹持管爆管原因分析[J]. 热力发电, 2012,41(2):88-90.

ZHAO Mingzhong, WU Kai Gansu Electric Power Science Research Institute. CAUSE ANALYSIS OF CONTINUOUS TUBE BURST ON HOLDING PIPES OF THE SCREEN-TYPE REHEATER FOR BOILER NO1 IN ONE POWER PLANT[J]. Thermal power generation, 2012, 41(2): 88-90.
赵明忠, 吴凯. 某电厂锅炉屏式再热器夹持管爆管原因分析[J]. 热力发电, 2012,41(2):88-90. DOI：

ZHAO Mingzhong, WU Kai Gansu Electric Power Science Research Institute. CAUSE ANALYSIS OF CONTINUOUS TUBE BURST ON HOLDING PIPES OF THE SCREEN-TYPE REHEATER FOR BOILER NO1 IN ONE POWER PLANT[J]. Thermal power generation, 2012, 41(2): 88-90. DOI：

摘要

对某电厂发电机组锅炉屏式再热器(屏再)夹持管连续多次爆管原因进行了分析

认为在焊接过程中未能严格执行焊接工艺要求

致使焊接接头的热影响区产生晶粒粗大和黑色网状晶界的不良组织

并且焊后热处理不当使熔合线产生了沿晶裂纹

这些裂纹在机组运行过程中逐渐扩展造成管子沿焊缝熔合线开裂。对此

建议加强设备监造

对重要的承压部件进行无损探伤抽检和理化性能试验。

Abstract

The causes leading to continuous and frequent tube bursts on holding pipes of screen-typ reheater for boiler no1 in one power plant have been analysed

it is believed that the requirements of welding process hadn't strictly implemented during the course of welding

resulting in bad structure of coase-grained and black-reticulated grain boundaries appeared in the heat affecting areas of welded joints.Owing to unsuitable heat treatment after welding

the along-crystalline cracks are occurred on fusion lines

these cracks expand in operation

resulting in rupture along fusion line of the welding joints on pipes.It is recommented to further strengthen the supervision in manufacturing the equipments

and to carry out non-destructive inspection and physico-chemical test for the important pressurized parts.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

18-8型奥氏体不锈钢锅炉管服役特性研究(六)

600MW机组锅炉减温器断裂原因分析及改进措施

珠海发电厂锅炉高温受热面管壁超温问题试验研究及解决方案

1000 MW机组蒸汽管道氧化皮吹扫工艺研究

HCM2S(T23)钢中的碳化物及其演化规律