超级马氏体不锈钢00Cr13Ni4Mo力学性能与抗磨蚀性能试验

发电技术论坛 | 更新时间：2025-09-28

- 超级马氏体不锈钢00Cr13Ni4Mo力学性能与抗磨蚀性能试验
- Mechanical properties and anti-abrasion performance of 00Cr13Ni4Mo super martensitic stainless steel
- 热力发电 2016年45卷第3期页码：110-115
- 作者机构：
  
  西安热工研究院有限公司
- 作者简介：
- 基金信息：
- DOI：
  中图分类号： TG142.71
- 纸质出版日期：2016
- 稿件说明：
移动端阅览
董方奇, 杨百勋, 李益民, 等. 超级马氏体不锈钢00Cr13Ni4Mo力学性能与抗磨蚀性能试验[J]. 热力发电, 2016,45(3):110-115.

DONG Fangqi, YANG Baixun, LI Yimin, et al. Mechanical properties and anti-abrasion performance of 00Cr13Ni4Mo super martensitic stainless steel[J]. Thermal power generation, 2016, 45(3): 110-115.
董方奇, 杨百勋, 李益民, 等. 超级马氏体不锈钢00Cr13Ni4Mo力学性能与抗磨蚀性能试验[J]. 热力发电, 2016,45(3):110-115. DOI：

DONG Fangqi, YANG Baixun, LI Yimin, et al. Mechanical properties and anti-abrasion performance of 00Cr13Ni4Mo super martensitic stainless steel[J]. Thermal power generation, 2016, 45(3): 110-115. DOI：

摘要

通过扫描电镜、透射电镜、硬度与冲击试验以及冲刷磨损试验

对超级马氏体不锈钢00Cr13Ni4Mo在8种不同热处理工艺下的力学性能与抗磨蚀性能进行了研究。结果表明:00Cr13Ni4Mo钢在550~650℃回火后产生逆变奥氏体

逆变奥氏体降低了材料的强度与硬度

增加了材料的韧性;00Cr13Ni4Mo钢的抗磨蚀性能主要与硬度有关

而与其冲击韧性关系较小;从材料性能和经济性综合考虑

00Cr13Ni4Mo钢最佳热处理工艺为1 050℃/9h正火+550℃/6h一次回火处理。

Abstract

The mechanical properties and anti-abrasion properties of 00Cr13Ni4 Mo super martensitic stainless steel under 8heat treatment processes were investigated

through a series of tests

such as scanning electron microscopy analysis

transmission electron microscopy analysis

hardness and impact test

and the erosion wear test.The results show that

the reverse austenite formed after the 00Cr13Ni4 Mo steel was tempered at 550℃to 650℃

which reduced the strength and hardness of the material and increased the toughness of the material.The anti-abrasion performance of the 00Cr13Ni4 Mo steel is primarily related to its hardness

while the material's toughness affected little.Comprehensively considering the properties and the economy

being normalized at 1 050 ℃for 9hand first tempered at 550 ℃for 6his the most suitable heat treatment process for this kind of steel.

关键词

Keywords

references

浏览量

314

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

WB36钢的热处理工艺及微观组织

HCM2S(T23)钢中的碳化物及其演化规律

18-8型奥氏体不锈钢锅炉管服役特性研究(六)

1.5D弯曲半径感应弯管的试验评定及应用

P91主蒸汽管道高硬度和低硬度焊缝性能研究