Influence of Annealing Atmosphere on the Ferroelectric and Leakage Current Behavior of Bi₂NiMnO₆ Thin Films

更新时间：2026-05-27

- Influence of Annealing Atmosphere on the Ferroelectric and Leakage Current Behavior of Bi₂NiMnO₆ Thin Films
- Vol. 32, Issue 4, Pages: 21-24(2015)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.1007-7162.2015.04.004
  CLC：
- Online First：04 December 2015，
  
  Published：2015
- 稿件说明：
移动端阅览
邓敏霖, 刘秋香, 李万朋. 不同退火气氛下Bi₂NiMnO₆薄膜的铁电性能和漏电流研究[J]. 广东工业大学学报, 2015, 32(4): 21-24. DOI: 10.3969/j.issn.1007-7162.2015.04.004.

Deng Min-lin, Liu Qiu-xiang, Li Wan-peng. Influence of Annealing Atmosphere on the Ferroelectric and Leakage Current Behavior of Bi₂NiMnO₆ Thin Films[J]. 2015, 32(4): 21-24. DOI: 10.3969/j.issn.1007-7162.2015.04.004.
邓敏霖, 刘秋香, 李万朋. 不同退火气氛下Bi₂NiMnO₆薄膜的铁电性能和漏电流研究[J]. 广东工业大学学报, 2015, 32(4): 21-24. DOI: 10.3969/j.issn.1007-7162.2015.04.004. DOI：

Deng Min-lin, Liu Qiu-xiang, Li Wan-peng. Influence of Annealing Atmosphere on the Ferroelectric and Leakage Current Behavior of Bi₂NiMnO₆ Thin Films[J]. 2015, 32(4): 21-24. DOI: 10.3969/j.issn.1007-7162.2015.04.004. DOI：

摘要

采用化学溶液法以LaNiO

为底电极在Si(100)衬底上生长了Bi

NiMnO

薄膜，分别在N

和O

下对薄膜进行退火，退火温度均为600 ℃，研究不同退火气氛对薄膜结构与电性能的影响.用XRD测量分析了Bi

NiMnO

薄膜的结构，用铁电性能测量仪表征了样品的铁电性能和漏电流特性.结果表明，在N

或O

气氛下，Bi

NiMnO

薄膜均能成相，所有样品在室温下均表现出铁电性能，同时，这些样品都呈现出相当低的漏电流密度.此外，还讨论了Bi

NiMnO

薄膜的导电机制.

Abstract

NiMnO

(abbreviated as BNMO) thin films grow on LaNiO

buffered Si(100) substrate prepared by chemical solution deposition. The structure of the thin films is characterized by X-ray diffraction

and both the ferroelectric properties and leakage current behavior are measured by ferroelectric tester at room temperature. The results suggest that they have become crystalline phases in the two samples annealed in N

and O

respectively. The ferroelectric properties appear in all samples under room temperature and the BNMO sample shows a fairly low leakage current density. Furthermore

the m

echanism of electrical conductivity is also investigated in the paper.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation and Characterization of Double Perovskite Sr2GdSbO6:Eu3+ Phosphor

The Structure Comparison of Bi-Si-B-O Sol-Gel and Melt-quenching Glass

Multi-Scale Contrastive Embedding Enhanced Adaptive Intrusion Detection Model

A Resource Allocation Optimization Method for Multi-UAV Integrated Sensing, Computing, and Communication Towards Disaster Relief

Bimodal Iterative Cross-attention Fusion Ensemble Framework

Related Author

Fang Zhi-xiong

Yi Shuang-ping

Zhou Yi-xuan

Zhao Wei-ren

Li Qian

Yuan Ge-cheng

Luo Zhi-jie

Deng Nan-lin

Related Institution

School of Physics and Optoelectronic Engineering, Guangdong University of Technology

AI问答

⁰

Influence of Annealing Atmosphere on the Ferroelectric and Leakage Current Behavior of Bi2NiMnO6 Thin Films

DOI：10.3969/j.issn.1007-7162.2015.04.004

摘要

Abstract

关键词

Keywords

references

Influence of Annealing Atmosphere on the Ferroelectric and Leakage Current Behavior of Bi₂NiMnO₆ Thin Films