Analysis on weld defects and tensile properties of dissimilar steel with backing plate

更新时间：2025-09-28

- Analysis on weld defects and tensile properties of dissimilar steel with backing plate
- Thermal Power Generation Vol. 52, Issue 1, Pages: 170-176(2023)
- 作者机构：
  
  1. 华能国际电力股份有限公司南通电厂
  2. 西安热工研究院有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.202205101
  CLC： TG441.7;TM621.2
- Published：2023
- 稿件说明：
移动端阅览
WANG Feng, LI Liang, XU Gang, et al. Analysis on weld defects and tensile properties of dissimilar steel with backing plate[J]. Thermal power generation, 2023, 52(1): 170-176.
DOI：

WANG Feng, LI Liang, XU Gang, et al. Analysis on weld defects and tensile properties of dissimilar steel with backing plate[J]. Thermal power generation, 2023, 52(1): 170-176. DOI： 10.19666/j.rlfd.202205101.

摘要

异种钢焊接是电厂锅炉受热面管广泛采用的一种连接方式。以某火电机组过热器出口段TP304H和T22为母材的带垫板异种钢焊接接头为研究对象，通过宏观测量、微观组织分析、EDS能谱检测和拉伸试验等研究，分析了焊接接头中裂纹的生成机理及影响。结果表明：3种材料热膨胀系数差异及应力集中是带垫板异种钢焊缝裂纹产生的诱因，裂纹在镍基焊缝填充材料中扩展；室温拉伸时焊缝是薄弱环节，而高温拉伸时熔合线和母材是断裂部位。

Abstract

Welding of dissimilar steels is a widely used connection method for super-heater tubes of boilers in power plants. Taking the TP304H/T22 dissimilar steel welded joint with backing plate at the superheater outlet of a thermal power unit as the research object

the formation mechanism and influence of cracks in the welded joint are analyzed through macro measurement

microstructure analysis

EDS energy spectrum detection and tensile test. The results show that

the differences in thermal expansion coefficients of the three substrates and stress concentration are the cause of the cracks of the dissimilar steel weld with backing plate and crack propagation in nickel base weld filler.The weld is the weak link in room temperature tension

while the fusion line and base metal are the fracture parts in high temperature tension.

关键词

Keywords

references

Views

107

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(5)

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(6)

STUDY ON SERVICING PROPERTIES OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(4)

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 AUSTENITIC STAINLESS STEEL(2)

TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL

Related Author

SHI Zhigang

MA Hong

ZHENG Fangping

HE Xipeng

ZHANG Lei

WANG Hongzhe Xi'an Thermal Power Research Institute Co Ltd

WANG Hongzhe

ZHANG Lei Xi'an Thermal Power Research Institute Co Ltd

Related Institution

Shanghai Electric Power University

Taiyuan University of Technology

Huaneng Shang'an Power Plant

Hebei Electric Power Research Institute

Huaneng Qinbei Power Generation Co., Ltd

AI问答

⁰