Study on CO oxidation performance of Ce-Cu/γ-Al<sub>2</sub>O<sub>3</sub> catalyst in flue gas

XIANG Xiaofeng; ZHANG Bo; ZHANG Xiangyu; LU Xu; XU Hongjie

doi:10.19666/j.rlfd.202012303

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Study on CO oxidation performance of Ce-Cu/γ-Al₂O₃ catalyst in flue gas

更新时间：2025-09-28

- Study on CO oxidation performance of Ce-Cu/γ-Al₂O₃ catalyst in flue gas
- Thermal Power Generation Vol. 50, Issue 10, Pages: 124-129(2021)
- 作者机构：
  
  西安热工研究院有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.202012303
  CLC： TQ426;X701
- Published：2021
- 稿件说明：
移动端阅览
XIANG Xiaofeng, ZHANG Bo, ZHANG Xiangyu, et al. Study on CO oxidation performance of Ce-Cu/γ-Al₂O₃ catalyst in flue gas[J]. Thermal power generation, 2021, 50(10): 124-129.
DOI：

XIANG Xiaofeng, ZHANG Bo, ZHANG Xiangyu, et al. Study on CO oxidation performance of Ce-Cu/γ-Al₂O₃ catalyst in flue gas[J]. Thermal power generation, 2021, 50(10): 124-129. DOI： 10.19666/j.rlfd.202012303.

摘要

采用传统浸渍法制备了Ce-Cu/γ-Al_2O_3非贵金属催化剂

基于深度分级燃烧炉膛外CO氧化催化作用

在管式炉实验平台上

开展低温CO氧化催化基础实验研究。结果表明:在250～300℃之间

催化氧化CO效果明显(255℃时CO转化率78.62%)

300℃之后保持较高CO转化率(大于99.5%);停留时间1.2 s时

在150～200℃就具有较高的CO氧化活性

延长到5 s后CO转化率55.7%(150℃)

很快增加到97%(200℃)

催化效果明显;对高体积分数CO(3 000×10~(–6))也具备较高的催化剂活性和处理能力;催化效率随气速(0.2～0.8 L/min)减小而增大;含氧量(体积分数2%～3%)越高

催化剂效率越高;添加Co后Al_2O_3衍射峰轻微下降

有利于催化氧化活性的提高。

Abstract

Based on the catalytic effect of CO oxidation outside the furnace of deep staged combustion

the experimental study on Ce-Cu/γ-Al_2O_3 non-precious metal catalyst prepared by conventional impregnation method was carried out in a tubular furnace.The results show that

the catalytic oxidation of CO was obvious at 250～300℃(the conversion rate of CO reached 78.62%at 255℃)

and the conversion rate of CO was maintained at a high level (99.5%) at temperatures higher than 300℃.When the residence time was 1.2 s

the CO oxidation activity was higher at 150～200℃.When the residence time was 5 s

the conversion rate of CO was 55.7%(150℃) and quickly increased to 97%(200℃)

with obvious catalytic effect.The catalyst also had high activity and treatment capacity for CO with high volume fraction (3 000×10~(–6)).The catalytic efficiency increased with the decrease of gas velocity (0.2～0.8 L/min) and the increase of oxygen content (2%～3%).The diffraction peak of Al_2O_3 decreased slightly after the addition of Co

which is beneficial to the improvement of catalytic oxidation activity.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Performance of Fe-Ce oxide denitration catalyst and its resistance to toxicity

Effects of alkali/alkaline earth metals on coal pyrolysis:research progress

APPLICATION OF SCR DENITRIFICATION TECHNOLOGY ONTO COAL-FIRED BOILERS IN CHINA

STUDY ON BEHAVIOR OF CATALYCTS FOR SCR DENITRIFICATION USING DIFFERENT TiO₂ AS CARRIER

THE OPERATION SITUATION OF CATALYST IN SCR DENITRIFICATION SYSTEM OF ONE THERMAL POWER PLANT

Related Author

ZHANG Guangxue

ZHOU Anqi

FAN Haiyan

WANG Jinqing

CHI Zuohe

CHEN Hongwei

ZHANG Zhiyuan

ZHAI Jianjun

Related Institution

Zhejiang Environmental Protection Science Design and Research Institute

College of Metrology and Testing Engineering, China Institute of Metrology

Chinalco Ningxia Energy Group Co., Ltd

Key Laboratory of Power Station Equipment Status Monitoring and Control, Ministry of Education, North China Electric Power University

Topso Company Beijing Representative Office

AI问答

⁰

Study on CO oxidation performance of Ce-Cu/γ-Al2O3 catalyst in flue gas

DOI：10.19666/j.rlfd.202012303

摘要

Abstract

关键词

Keywords

references

Study on CO oxidation performance of Ce-Cu/γ-Al₂O₃ catalyst in flue gas