Experiment of fracture characteristics of 10Cr rotor steel used in 600℃ USC steam turbines

更新时间：2025-09-28

- Experiment of fracture characteristics of 10Cr rotor steel used in 600℃ USC steam turbines
- Thermal Power Generation Vol. 47, Issue 6, Pages: 64-70(2018)
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 哈尔滨汽轮机厂有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201712156
  CLC： TG142.73
- Published Online：06 June 2018，
  
  Published：2018
- 稿件说明：
移动端阅览
YANG Baixun, TIAN Xiao, XU Hui, et al. Experiment of fracture characteristics of 10Cr rotor steel used in 600℃ USC steam turbines[J]. Thermal power generation, 2018, 47(6): 64-70.
DOI：

YANG Baixun, TIAN Xiao, XU Hui, et al. Experiment of fracture characteristics of 10Cr rotor steel used in 600℃ USC steam turbines[J]. Thermal power generation, 2018, 47(6): 64-70. DOI： 10.19666/j.rlfd.201712156.

摘要

为全面了解国产和进口10Cr转子钢的性能差异

本文对其化学成分和力学性能进行了测试

并采用紧凑拉伸试样测试了其在室温和高温(600℃)下的断裂韧度(KIC)

分析了国产和进口10Cr转子钢的断裂韧度与其冲击吸收能量(KV_2)和韧脆转变温度(FATT50)之间的关系。结果表明:国产10Cr转子钢的化学成分中P、Si、Cu、Sn含量比进口10Cr转子钢略高

微观组织观察发现国产10Cr转子钢存在较多的粒度在600~700 nm的颗粒状富Nb相;国产和进口10Cr转子钢的拉伸强度基本相当

国产10Cr转子钢的室温冲击吸收能量明显低于进口10Cr转子钢

其高温延伸率略低于进口10Cr转子钢;相对于进口10Cr转子钢

国产10Cr转子钢的KV_2偏低、FATT50偏高

且KIC明显低。

Abstract

To comprehensively understand the domestic and imported 10Cr rotor steels

the chemical compositions and mechanical properties are tested in this study

and the fracture toughness(KIC) is also tested at room temperature and high temperature(600 ℃) using compact tensile specimens. Meanwhile

the relationship among the fracture toughness

impact absorbed energy(KV_2) and ductile-brittle transition temperature(FATT50)of the domestic and imported 10Cr rotor steels are analyzed. The results show that the content of P

Si

Cu and Sn in the domestic 10Cr rotor steel is slightly higher than that in the imported 10Cr rotor steel. The microstructure observes that the domestic 10Cr rotor steel has more granular Nb phase with a grain size of 600~700 nm. The domestic and imported 10Cr rotor steels have similar tensile strengths. However

the KV2 of the domestic 10Cr rotor steel at room temperature is obviously lower than that of the imported 10Cr rotor steel

and the high-temperature elongation of the domestic 10Cr rotor steel is slightly lower than that of the imported 10Cr rotor steel. Compared with the imported 10Cr rotor steel

the domestic 10Cr rotor steel has lower KV_2

higher FATT50

and lower KIC.

关键词

Keywords

references

0

Views

124

下载量

0

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Related Articles

Development and expectation of application of ultra-supercritical double-reheat steam turbines

Economy analysis for an ultra supercritical 1 000 MW unit with EC-BEST thermal dynamic system

SIMPLIFIED FINITEELEMENT CALCULATION MODEL OF TEMPERATURE FIELD FOR STEAM TURBINE ROTOR

APPLICATION OF SOLID SELF-LUBRICATING TECHNOLOGY IN POWER PLANTS

STUDY ON CONTROL SYSTEM SETTING OF DOUBLE EXTRACTION ADJUSTABLE STEAM TURBINE

Related Author

WANG Jianlu

ZHANG Xiaodong

HOU Mingjun

PEI Dongsheng

BAO Weiwei

LIU Shilei

LUO Juan

HU Niansu

Related Institution

Dongfang Electric Corporation Dongfang Turbine

Huaneng Suzhou Thermal Power Co., Ltd

Wuhan University

Zhangze Power Plant

AI问答

⁰