Experment of the corrosion behavior of Super304H steel in simulative coal ash/flue gas environment at 650℃

LIU Wu; LU Jintao; HUANG Jinyang; DANG Yingying; ZHAO Xinbao; ZHAO Maiqun; YUAN Yong

doi:10.19666/j.rlfd.201708167

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Experment of the corrosion behavior of Super304H steel in simulative coal ash/flue gas environment at 650℃

更新时间：2025-09-28

- Experment of the corrosion behavior of Super304H steel in simulative coal ash/flue gas environment at 650℃
- Thermal Power Generation Vol. 47, Issue 6, Pages: 78-84(2018)
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 西安理工大学材料科学与工程学院
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201708167
  CLC： TG174
- Published Online：06 June 2018，
  
  Published：2018
- 稿件说明：
移动端阅览
LIU Wu, LU Jintao, HUANG Jinyang, et al. Experment of the corrosion behavior of Super304H steel in simulative coal ash/flue gas environment at 650℃[J]. Thermal power generation, 2018, 47(6): 78-84.
DOI：

LIU Wu, LU Jintao, HUANG Jinyang, et al. Experment of the corrosion behavior of Super304H steel in simulative coal ash/flue gas environment at 650℃[J]. Thermal power generation, 2018, 47(6): 78-84. DOI： 10.19666/j.rlfd.201708167.

摘要

采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、X射线能谱仪(EDS)、电子背散射衍射(EBSD)等方法研究了18-8系奥氏体钢Super304H在650℃模拟烟气侧环境中高温腐蚀行为。结果表明:Super304H钢试片腐蚀70、150、320和700 h后

腐蚀层的平均厚度分别为2.5、5.2、11.5和27.8mm;腐蚀层外层主要为疏松的Fe_2O_3

内层为相对致密的Cr_2O_3和内硫化产物。腐蚀150 h以后

试片表面保护性的Cr_2O_3膜逐渐剥落

内硫化产物在晶界处累积并膨胀

随着Fe向氧化膜扩散、溶解并继续向氧化膜外扩散

生成"瘤状"Fe_2O_3

最终成为多层的凸起腐蚀产物。随着腐蚀时间的延长

"瘤状"腐蚀产物粒径逐渐增大至10mm以上

更易破裂、剥落的腐蚀层导致试片的抗腐蚀性不断下降。

Abstract

The high temperature corrosion behavior of 18-8 Austenitic Super304H in coal ash/flue gas environment at 650 ℃ is investigated by means of XRD

SEM

EDS and EBSD and so on. The results show that

after corrosion for 70

150

320 and 700 h

the average thickness of corrosion layer are 2.5

5.2

11.5 and 27.8 mm

respectively. The corrosion layer is mainly composed of loose Fe_2O_3 at outer layer and dense Cr_2O_3 and internal vulcanization products at inner layer. After corrosion for 150 h

the protective Cr_2O_3 layer gradually desquamates and internal vulcanization products accumulate and then expand at the grain boundary. With the diffusion and dissolution of Fe to the outside of oxide film

a "nodular" Fe_2O_3 is formed and finally becomes a multilayered raised corrosion product. With the increase of corrosion time

the size of the "nodular" corrosion products gradually increases to more than 10 mm and the corrosion layer is more likely to rupture and peel off

which decreases the corrosion resistance of the alloy.

关键词

Keywords

references

Views

127

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON PERFORMANCE OF CORROSIONPRVENTING AND WEARRESISTING COATINGS ON “TUBES OF FOUR KINDS” IN THE BOILER

CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF

CAUSE ANALYSIS OF SERIOUS HIGH TEMPERATURE CORROSION AND HIGH CONTENT OF UNBURNED COMBUSTIBLES IN FLY ASH UNDER LOW LOAD OF ONE WALL-FIRING BOILER

CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION ON WATER WALL OF SUPERCRITICAL ONCE-THROUGH BOILERS AND COUNTERMEASURES THEREOF

STUDY ON WASTE SOLUTION TREATMENT FOR COMPOSITE ORGANIC ACID CLEANING

Related Author

YANG Hui

ZHANG Guo-bing

MU Chun-hua1

ZHANG Yi-zheng1

WANG Chun-chang21.Huaneng Rizhao Power Plant

ZHONG Wan-li

WU Shi-deng

ZENG Fan-yun Guangdong Electric Power Science Research Institute

Related Institution

Second Artillery Engineering College

Hejin Power Plant

Huaneng Rizhao Power Plant

Guangdong Electric Power Research Institute

Zhejiang Zheneng Power Generation Co., Ltd

AI问答

⁰