Nanostructured ceramic coating technology in a W-flame boiler burning high-sulfur coal

更新时间：2025-09-28

- Nanostructured ceramic coating technology in a W-flame boiler burning high-sulfur coal
- Thermal Power Generation Vol. 47, Issue 3, Pages: 88-93(2018)
- 作者机构：
  
  1. 中电华创电力技术研究有限公司
  2. 西安热工研究院有限公司
  3. 兆山科技(北京)有限公司
  4. 四川中电福溪电力开发有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201708133
  CLC： TK08
- Published Online：07 March 2018，
  
  Published：2018
- 稿件说明：
移动端阅览
LI Guangwei, MENG Yi, NING Xinyu, et al. Nanostructured ceramic coating technology in a W-flame boiler burning high-sulfur coal[J]. Thermal power generation, 2018, 47(3): 88-93.
DOI：

LI Guangwei, MENG Yi, NING Xinyu, et al. Nanostructured ceramic coating technology in a W-flame boiler burning high-sulfur coal[J]. Thermal power generation, 2018, 47(3): 88-93. DOI： 10.19666/j.rlfd.201708133.

摘要

为解决燃用高硫煤W火焰锅炉受热面发生的高温硫腐蚀、冲蚀磨损与沾污结渣等共性问题

提出施用ZST高温纳米陶瓷材料进行防腐、防磨、防结渣处理。本文阐述了ZST高温纳米陶瓷表面材料的性能指标和技术特点

以及喷涂施工工艺

并在某电厂燃用高硫煤W火焰锅炉受热面上进行了喷涂试验。喷涂后的受热面经4 000 h现场服役

涂层表面完好

宏观检查和微观检测分析结果表明

该纳米陶瓷涂层具有优异的耐腐、抗磨和防结渣的作用。

Abstract

In order to solve the problems occurred on heating surfaces of W-flame boilers firing high sulfur content coal

such as high temperature sulfur corrosion

solid-particle erosion and fouling and slagging

the ZST high temperature nanostructured ceramic coating technique was proposed to prevent the heating surface from corrosion

abrasion and slagging. The performance and features of the ZST high temperature nanostructured ceramic coating material are described. Moreover

spraying test was carried out on heating surface of a W-flame boiler firing highsulfur content coal. The results show that

spalling of the nanostructured ceramic coating didn't occur after 4 000 hours' in-service

indicating this nano-ceramic coating has excellent performance in corrosion resistance

wear resistance and slagging resistance.

关键词

Keywords

references

Views

194

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

INFLUENCE OF HIGH-SODIUM COAL UPON SLAGGING,CONTAMINATION,AND CORROSION ON THE HEATING SURFACE OF BOILERS

Experimental research on co-firing high suffer content coals in bituminite-fired boiler

Experimental study on combustion performance of high moisture lignite before and after drying

CAUSES LEADING TO SLAGGING IN FURNACE OF TANGENTIAL FIRING PULVERIZED COAL BOILER AND PREVENTIVE MEASURES THEREOF

A PREDICTION METHOD OF SLAGGING BEHAVIOR FOR PULVERIZED COAL BY USING TEST METHOD OF SEDIMENDATION FURNACE

Related Author

DONG Ming-gang Hongsheng Electricity and Heat Company under Jiuqun Iron and Steel Corporation

AI Chenhui

DU Jiajun

GUO Qianxin

CAO Zhongyou

BAI Yang

ZHAO Yonggang

XIANG Xiaofeng

Related Institution

Jiugang Hongsheng Electric Heating Company

Shenhua Sichuan Energy Co., Ltd

Shenhua Shendong Electric Power Co., Ltd

Guoneng Baoqing Coal and Electricity Co., Ltd

Shajiao C Power Plant

AI问答

⁰