STUDY ON DIAGNOSIS AND MECHANISMS OF FAILURE RESULTED FROM CORROSION FATIGUE ON MEMBRANE WATER-WALL TUBES

SHI Zhi-gang1; MA Hong1; LI Wei2; SUN Lei2; HE Xi-peng1; ZHANG Lei11.Xi'an Thermal Power Research Institute Co Ltd

doi:10.19666/j.rlfd.2008.05.021

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

STUDY ON DIAGNOSIS AND MECHANISMS OF FAILURE RESULTED FROM CORROSION FATIGUE ON MEMBRANE WATER-WALL TUBES

更新时间：2025-09-28

- STUDY ON DIAGNOSIS AND MECHANISMS OF FAILURE RESULTED FROM CORROSION FATIGUE ON MEMBRANE WATER-WALL TUBES
- Thermal Power Generation Issue 5, Pages: 77-80(2008)
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 国电太原第一热电厂
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2008.05.021
  CLC： TK224.9
- Published：2008
- 稿件说明：
移动端阅览
SHI Zhi-gang1, MA Hong1, LI Wei2, et al. STUDY ON DIAGNOSIS AND MECHANISMS OF FAILURE RESULTED FROM CORROSION FATIGUE ON MEMBRANE WATER-WALL TUBES[J]. Thermal power generation, 2008, (5): 77-80.
DOI：

SHI Zhi-gang1, MA Hong1, LI Wei2, et al. STUDY ON DIAGNOSIS AND MECHANISMS OF FAILURE RESULTED FROM CORROSION FATIGUE ON MEMBRANE WATER-WALL TUBES[J]. Thermal power generation, 2008, (5): 77-80. DOI： 10.19666/j.rlfd.2008.05.021.

摘要

腐蚀疲劳是锅炉水冷壁管水侧常见的失效类型

其隐蔽性强

破坏性大

严重威胁电厂的安全生产。从某电厂锅炉膜式水冷壁管频繁开裂的实例出发

介绍了水冷壁管腐蚀疲劳失效的特征

分析了疲劳失效的原因及易产生疲劳失效的部位

并提出了降低交变应力和减少腐蚀源等防止对策。

Abstract

The corrosion fatigue is a kind of failure commonly occurred on the water side of water-wall tubes in boiler

having strong covertness and large damaging force

threatening seriously safe production in power plants.From practical example of frequently cracking on membrane water-wall tubes in boilers of one power plant

the characteristics of corrosion fatigue failure of water-wall tubes have been presented

the causes and locations easily resulting in fatigue failure being analyzed

and preventing measures

such as lowering the alternating stress

and decreasing the corrosion source etc.

have been put forward.

关键词

Keywords

references

Views

153

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF

CAUSE ANALYSIS OF SLAGGING IN BABCOCK 2209 t/h BOILERS MADE IN GERMANY AND PREVENTION THEREOF

ESTABLISHMENT OF SERVICE LIFE MANAGEMENT SYSTEM FOR HIGH-TEMPERATURE BOILER TUBES IN THERMAL POWER PLANT BASED ON B/S STRUCTURE

ANTI-WEAR TECHNOLOGY FOR CFB BOILERS

CAUSE ANALYSIS OF HIGH-TEMPERATURE CORROSION ON WATER-WALL OF A 440 t/h BOILER

Related Author

ZHANG Guo-bing

LIANG Gui-long

LI Hu

DU Bao-hua

LI Yao-jun

LIU Zhen-yu

LI Chung-min

WANG Zhong-jie

Related Institution

Hejin Power Plant

Huaneng Dezhou Power Plant

Huaneng Yuhuan Power Plant

Henan Zhongfu Electric Power Co., Ltd

Henan Thermal Power Construction First Company

AI问答

⁰