ANTI-WEAR TECHNOLOGY FOR CFB BOILERS

QIAN Yu1; ZHANG Min2; LI Li-quan31.Branch Company No.2 under Henan Nanfu Electric Power Co Ltd

doi:10.19666/j.rlfd.2007.06.019

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

ANTI-WEAR TECHNOLOGY FOR CFB BOILERS

更新时间：2025-09-28

- ANTI-WEAR TECHNOLOGY FOR CFB BOILERS
- Thermal Power Generation Issue 6, Pages: 72-74(2007)
- 作者机构：
  
  1. 河南中孚电力有限公司
  2. 西安热工研究院有限公司
  3. 河南省火电建设一公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2007.06.019
  CLC： TK229.6
- Published：2007
- 稿件说明：
移动端阅览
QIAN Yu1, ZHANG Min2, LI Li-quan31.Branch Company No.2 under Henan Nanfu Electric Power Co Ltd. ANTI-WEAR TECHNOLOGY FOR CFB BOILERS[J]. Thermal power generation, 2007, (6): 72-74.
DOI：

QIAN Yu1, ZHANG Min2, LI Li-quan31.Branch Company No.2 under Henan Nanfu Electric Power Co Ltd. ANTI-WEAR TECHNOLOGY FOR CFB BOILERS[J]. Thermal power generation, 2007, (6): 72-74. DOI： 10.19666/j.rlfd.2007.06.019.

摘要

针对大容量循环流化床(CFB)锅炉磨损严重的问题

分析了磨损的形式和产生磨损的原因

并从设备改造角度提出了一些防磨措施。实践证明

这些防磨措施效果比较理想

可有效地减轻CFB锅炉的磨损。

Abstract

Directing against serious wear-out problems occurred on large-capacity circulating fluidized bed (CFB) boilers

the wearing mode and causes leading to wear-out have been analysed

and some anti-wear measures being put forward from view point of retrofitting the equipments. The practice proves that the effectiveness of said measures are comparatively perfect

can effectively alleviate wear-out on CFB boilers.

关键词

Keywords

references

Views

220

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF

CAUSE ANALYSIS OF SLAGGING IN BABCOCK 2209 t/h BOILERS MADE IN GERMANY AND PREVENTION THEREOF

ESTABLISHMENT OF SERVICE LIFE MANAGEMENT SYSTEM FOR HIGH-TEMPERATURE BOILER TUBES IN THERMAL POWER PLANT BASED ON B/S STRUCTURE

CAUSE ANALYSIS OF HIGH-TEMPERATURE CORROSION ON WATER-WALL OF A 440 t/h BOILER

CAUSE ANALYSIS OF FREQUENT BURST-LEAKAGE OCCURRED ON REHEATER AND WATER-WALL OF 300 MW UTILITY BOILER

Related Author

ZHANG Guo-bing

LIANG Gui-long

LI Hu

DU Bao-hua

LI Yao-jun

LIU Zhen-yu

LI Chung-min

WANG Zhong-jie

Related Institution

Hejin Power Plant

Huaneng Dezhou Power Plant

Huaneng Yuhuan Power Plant

Heze Power Plant

Huadian Pucheng Power Plant

AI问答

⁰