CAUSE ANALYSIS OF DESUPERHEATER FRACTURE FOR BOILER OF 600 MW UNIT

LIU Feng; YAN Kai-ping; TONG Ya-feng; JIA Ying-fan(Datang Panshan Power Generation Co Ltd

doi:10.19666/j.rlfd.2007.05.026

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF DESUPERHEATER FRACTURE FOR BOILER OF 600 MW UNIT

更新时间：2025-09-28

- CAUSE ANALYSIS OF DESUPERHEATER FRACTURE FOR BOILER OF 600 MW UNIT
- Thermal Power Generation Issue 5, Pages: 87-88(2007)
- 作者机构：
  
  大唐盘山发电有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2007.05.026
  CLC： TK223
- Published：2007
- 稿件说明：
移动端阅览
LIU Feng, YAN Kai-ping, TONG Ya-feng, et al. CAUSE ANALYSIS OF DESUPERHEATER FRACTURE FOR BOILER OF 600 MW UNIT[J]. Thermal power generation, 2007, (5): 87-88.
DOI：

LIU Feng, YAN Kai-ping, TONG Ya-feng, et al. CAUSE ANALYSIS OF DESUPERHEATER FRACTURE FOR BOILER OF 600 MW UNIT[J]. Thermal power generation, 2007, (5): 87-88. DOI： 10.19666/j.rlfd.2007.05.026.

摘要

分析了某电厂600 MW机组锅炉过热器减温器断裂的原因

认为其主要是减温水引进管与喷雾管壁温温差大、减温器入口管座与入口管的焊接缺陷以及喷雾管与入口管异种钢焊接存在弊端等。对此

提出了更换材质、减少壁厚、改进焊接和检验方法等措施

实施后

没有再出现减温水管道振动及其它异常现象

设备运行稳定。

Abstract

The causes leading to desuperheater fracture of boiler's superheater for 600 MW unit of one power plant have been analysed

it is believed that the main causes are as follows: large temperature difference between wall temperature of leading-in pipe and that of atomizing tube for the desuperheating water

welding defects of the inlet tube socket with the inlet tube of desuperheater

as well as malpractice existing in weldjoint of different steels for the atomizing tube and the inlet tube etc..For these

measures such as changing the quality of materials

decreasing the thickness of tube-wall

improving the welding technology and the detecting method etc.have been put forward.After implementation

vibration and other abnormalities of the desuperheating water pipeline have never occurred again

equipements are in stable operation.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

CAUSE ANALYSIS OF LOAD BEING LIMITED FOR ONE BOILER

Modification of secondary stage desuperheater for superheater in a 1025t/h boiler

CALCULATION OF WALL-TEMPERATURE FOR SUPERHEATER AND REHEATER OF HG670/13.7-YM13 TYPE BOILER

ANALYSIS AND TREATMENT OF SOMEWHAT LOWER MAIN STEAM TEMPERATURE PROBLEM FOR 2045 t/h BOILER

ESTABLISHMENT OF SERVICE LIFE MANAGEMENT SYSTEM FOR HIGH-TEMPERATURE BOILER TUBES IN THERMAL POWER PLANT BASED ON B/S STRUCTURE

Related Author

WANG Zhi-gang

ZHANG Guang-cai

WANG Chun-chang

WANG Xiao-xu

HAN YingXi’an Thermal Power Research Institute Co Ltd

HUANG Junjie

LIU Tong

XU Gang

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Guangzhou Hengyun Thermal Power (D) Factory Co., Ltd

North China Electric Power University

North China Electric Power University Beijing

AI问答

⁰