TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL

L Ping1; GUO Lei1; ZHAO Xian-ping2; TANG Bin1(1.Taiyuan University of Science & Technology

doi:10.19666/j.rlfd.2007.04.028

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL

更新时间：2025-09-28

- TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL
- Thermal Power Generation Issue 4, Pages: 97-99(2007)
- 作者机构：
  
  1. 太原理工大学
  2. 上海电力学院
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2007.04.028
  CLC： TK225
- Published：2007
- 稿件说明：
移动端阅览
L Ping1, GUO Lei1, ZHAO Xian-ping2, et al. TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL[J]. Thermal power generation, 2007, (4): 97-99.
DOI：

L Ping1, GUO Lei1, ZHAO Xian-ping2, et al. TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL[J]. Thermal power generation, 2007, (4): 97-99. DOI： 10.19666/j.rlfd.2007.04.028.

摘要

主要研究20碳钢表面经过碳-氮共渗热处理后在250℃~500℃的温度范围内受飞灰磨损的规律。试验结果表明

经过表面碳-氮共渗热处理后的20碳钢在试验温度范围内

仍然具有未处理时的热态磨损规律

即随温度的升高

相对磨损量先减小而后增大

临界温度为331℃。20碳钢经C-N共渗后相对磨损量减小一倍左右。

Abstract

The regularity of fly ash erosion on the surface of 20 carbon steel after heat treatment of carbonitriding

in a temperatre range of 250 ℃～500 ℃

has been mainly studied

results show that the 20 carbon steel after surface heat treatment by carbonitriding still has hot state erosion regularity before said treatment in the test temperature range

i.e.along with the temperature rise

the relative erosion rate decreases at first

and then increases

the critical temperature to be 330 ℃.After carbonitriding

the relative erosion rate of 20 carbon steel decreases about a half.

关键词

Keywords

references

Views

141

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(6)

THE CARBIDE CONTAINED IN HCM25(T23) STEEL AND EVOLUTION REGULARITY THEREOF

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(5)

STUDY ON SERVICING PROPERTIES OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(4)

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 AUSTENITIC STAINLESS STEEL(2)

Related Author

MA Hong

ZHANG Lei

ZHENG Fangping

HE Xipeng

SHI Zhigang

WANG Hongzhe Xi'an Thermal Power Research Institute Co Ltd

ZHANG Hongjun1 1.Xi'an Thermal Power Research Institute Co.Ltd.

TANG Liying1

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Guangdong Power Grid Corporation Electric Power Science Research Institute

Yangzi Petrochemical Shaoer Pipe Industry Co., Ltd

Nanjing University of Technology

Huaneng Shang'an Power Plant

AI问答

⁰