ANALYSIS OF CRACK DEFECT OCCURRED ON STEAM CONDUIT OF DESUPERHEATING WATER FOR BOILER SUPERHEATER OF 600 MW UNIT

doi:10.19666/j.rlfd.2006.12.019

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

ANALYSIS OF CRACK DEFECT OCCURRED ON STEAM CONDUIT OF DESUPERHEATING WATER FOR BOILER SUPERHEATER OF 600 MW UNIT

更新时间：2025-09-28

- ANALYSIS OF CRACK DEFECT OCCURRED ON STEAM CONDUIT OF DESUPERHEATING WATER FOR BOILER SUPERHEATER OF 600 MW UNIT
- Thermal Power Generation Issue 12, Pages: 58-61(2006)
- 作者机构：
  
  平圩发电有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2006.12.019
  CLC： TK223.32
- Published：2006
- 稿件说明：
移动端阅览
ANALYSIS OF CRACK DEFECT OCCURRED ON STEAM CONDUIT OF DESUPERHEATING WATER FOR BOILER SUPERHEATER OF 600 MW UNIT[J]. Thermal power generation, 2006, (12): 58-61.
DOI：

ANALYSIS OF CRACK DEFECT OCCURRED ON STEAM CONDUIT OF DESUPERHEATING WATER FOR BOILER SUPERHEATER OF 600 MW UNIT[J]. Thermal power generation, 2006, (12): 58-61. DOI： 10.19666/j.rlfd.2006.12.019.

摘要

介绍了600 MW机组锅炉过热器减温水系统联箱导汽管存在的问题

分析了其产生裂纹的原因

提出了合理的处理措施和修复工艺

可为电站设备构件失效的预防和处理提供借鉴。

Abstract

The problems existing in header’s steam conduit of desuperheating water ssytem for boiler superheater of 600 MW unit have been presented

the causes leading to cracks being analysed

scientific and reasonable remedial measures as well as repair technology being put forward

providing with reference for preventing and remedying component failure of equipments in power plants.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

CAUSE ANALYSIS OF CRACKS OCCURRED IN ANGLE-WELDING SEAM ON INLET HEADER OF LOW-TEMPERATURE SUPERHEATER

ANALYSIS AND INVESTIGATION ON CIRCUMFERNTIAL CRACKING OF PLATEN SUPERHEATER TUBES

A FLOW RATE CALCULATION METHOD FOR U- OR Z-SHAPED HEADERS

Effect of oxygenated treatment on oxide scale exfloliation

Experimental study on high temperature corrosion of T92 steel used for superheater of ultra supercritical unit boilers

Related Author

HU Xin-fang1

YUE Zeng-wu1

YU Guang-qiang2

WANG Jin-hai2

LIU Guo-gang2 1.Shandong Electric Power Reseach Institute

赵永宁

岳增武

胡新芳

Related Institution

Huaneng Dezhou Power Plant

Shandong Electric Power Research Institute

Guangdong Electric Power Test and Research Institute Guangzhou

Xi’an Thermal Power Research Institute Co., Ltd.

AI问答

⁰