STUDY ON MICROSTRUCTURE AGING OF T91 STEEL DURING PROCESS OF LONG-TERM OPERATION

SHI Zhi-gang; HOU An-zhu; LI Yi-min

doi:10.19666/j.rlfd.2006.04.020

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

STUDY ON MICROSTRUCTURE AGING OF T91 STEEL DURING PROCESS OF LONG-TERM OPERATION

更新时间：2025-09-28

- STUDY ON MICROSTRUCTURE AGING OF T91 STEEL DURING PROCESS OF LONG-TERM OPERATION
- Thermal Power Generation Issue 4, Pages: 54-58(2006)
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 渭河发电有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2006.04.020
  CLC： TG115.5
- Published：2006
- 稿件说明：
移动端阅览
SHI Zhi-gang, HOU An-zhu, LI Yi-min. STUDY ON MICROSTRUCTURE AGING OF T91 STEEL DURING PROCESS OF LONG-TERM OPERATION[J]. Thermal power generation, 2006, (4): 54-58.
DOI：

SHI Zhi-gang, HOU An-zhu, LI Yi-min. STUDY ON MICROSTRUCTURE AGING OF T91 STEEL DURING PROCESS OF LONG-TERM OPERATION[J]. Thermal power generation, 2006, (4): 54-58. DOI： 10.19666/j.rlfd.2006.04.020.

摘要

对两个电厂锅炉的T91钢制高温过热器和中温再热器管运行后微观组织的老化进行了试验研究。结果表明:光学显微镜下

难以观察到材料微观组织的老化特征;在透射电镜下

可明显观察到材料微观组织老化的精细结构;运行时间短的中温再热器管的微观组织老化较运行时间长的高温过热器管严重。

Abstract

A test study has been carried out for the microstructure aging of high-temperature surperheater and medium -temperature reheater tubes made from T91 steel for two utility boilers. Results show that the characteristics of microsturcture aging of the materials are difficult to be observed under an optical microscope; but the fine structure of microstructure aging can be obviously observed under a transmission electron microscope(TEM). The microstructure aging of medium-temperature reheater tubes during short-term operation is more serious than that of high-temperature superheater tubes during long-term operation.

关键词

Keywords

references

Views

399

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

CAUSE ANALYSIS OF WELDED SEAM CRACKING OCCURRED ON TUBES OF T91/TP34H HIGH-TEMPERATURE REHEATER

MICROSTRUCTURE AND FORMATION MECHANISM OF OXIDE FILM ON THE STEAM SIDE OF T91 STEEL AFTER HIGH TEMPERATURE OPERATION

DUCTILITY AND TOUGHNESS VARYING TENDENCY OF T91-STEEL AFTER LONG-TIME OPERATING AT HIGH TEMPERTURE

Related Author

ZHEGN Fangping

MA Hong

WANG Hongzhe

WANG Bilei Xi'an Thermal Power Research Institute Co Ltd

ZHONG Wanli1

LI Zhenggang2

WANG Wei1

YANG Bing2 1.Electric Power Science Research Institute under Guangdong Power Grid Corp

Related Institution

Guangdong Power Grid Corporation Electric Power Science Research Institute

School of Power and Mechanical Engineering, Wuhan University

Hebei Electric Power Science Research Institute

AI问答

⁰