CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF

ZHANG Guo-bing

doi:10.19666/j.rlfd.2006.03.009

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF

更新时间：2025-09-28

- CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF
- Thermal Power Generation Issue 3, Pages: 30-32(2006)
- 作者机构：
  
  河津发电厂
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2006.03.009
  CLC： TK224.9
- Published：2006
- 稿件说明：
移动端阅览
ZHANG Guo-bing. CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF[J]. Thermal power generation, 2006, (3): 30-32.
DOI：

ZHANG Guo-bing. CAUSE ANALYSIS OF HIGH TEMPERATURE CORROSION OCCURRED ON THE WATER-WALL AND RESOLUTION MEASURES THEREOF[J]. Thermal power generation, 2006, (3): 30-32. DOI： 10.19666/j.rlfd.2006.03.009.

摘要

对河津电厂2×350MW机组锅炉水冷壁产生高温腐蚀的原因进行了分析

认为其主要是主燃烧器区二次风和上部AA风分配不合理

造成主燃烧器区二次风不足所致。对此

提出了降低锅炉负荷、改善入炉煤质、加强主燃烧器区域二次风等解决办法。

Abstract

The causes leading to high temperature corrosion on water-wall of boilers for 2×350 MW units in first-phase project of Hejin Power Plant have been analysed. It is believed that the main cause is result of unreasonable distribution of the secondary air and upper AA air in the region of main burners

making secondary air in the said region to be insufficient. For this reason

resolution measures

such as reducing boiler’s load

improving quality of as-fired coal

strengthening secondary air in the region of main burners etc.

have been put forward.

关键词

Keywords

references

Views

168

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

CAUSE ANALYSIS OF SLAGGING IN BABCOCK 2209 t/h BOILERS MADE IN GERMANY AND PREVENTION THEREOF

ESTABLISHMENT OF SERVICE LIFE MANAGEMENT SYSTEM FOR HIGH-TEMPERATURE BOILER TUBES IN THERMAL POWER PLANT BASED ON B/S STRUCTURE

DISTRIBUTION OF TRACE ELEMENTS IN EMISSIION FROM COAL-WATER-SLURRY FIRED BOILERS

ANTI-WEAR TECHNOLOGY FOR CFB BOILERS

CAUSE ANALYSIS OF HIGH-TEMPERATURE CORROSION ON WATER-WALL OF A 440 t/h BOILER

Related Author

LIANG Gui-long

LI Hu

DU Bao-hua

LI Yao-jun

LIU Zhen-yu

LI Chung-min

WANG Zhong-jie

SUN Xi(Xi'an Thermal Power Reseach Institute Co.Ltd

Related Institution

Huaneng Dezhou Power Plant

Huaneng Yuhuan Power Plant

Xi'an Thermal Power Research Institute Co., Ltd

Zhejiang University

浙江大学

AI问答

⁰