CAUSE ANALYSIS OF WELDED SEAM CRACKING FOR COMB-SHAPED SEAL PASSING THROUGH THE ROOF OF REHEATER

doi:10.19666/j.rlfd.2003.12.018

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF WELDED SEAM CRACKING FOR COMB-SHAPED SEAL PASSING THROUGH THE ROOF OF REHEATER

更新时间：2025-09-28

- CAUSE ANALYSIS OF WELDED SEAM CRACKING FOR COMB-SHAPED SEAL PASSING THROUGH THE ROOF OF REHEATER
- Thermal Power Generation Issue 12, Pages: 50-52(2003)
- 作者机构：
  
  1. 湛江发电厂
  2. 湛江发电厂,广东,湛江,524099
  3. ,广东,湛江,524099
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2003.12.018
  CLC： TK225
- Published：2003
- 稿件说明：
移动端阅览
CAUSE ANALYSIS OF WELDED SEAM CRACKING FOR COMB-SHAPED SEAL PASSING THROUGH THE ROOF OF REHEATER[J]. Thermal power generation, 2003, (12): 50-52.
DOI：

CAUSE ANALYSIS OF WELDED SEAM CRACKING FOR COMB-SHAPED SEAL PASSING THROUGH THE ROOF OF REHEATER[J]. Thermal power generation, 2003, (12): 50-52. DOI： 10.19666/j.rlfd.2003.12.018.

摘要

针对DG1 0 2 5 /1 8.2Ⅱ (3)型锅炉中、高温再热器管与梳形密封板焊缝经常发生开裂泄漏问题

对其密封结构及裂纹断口进行了宏观、微观分析

认为其失效原因为结构几何应力作用下的蠕变失效

断裂类型为楔形蠕变断裂。对此

可采取改变梳形密封板与管子焊接结构方式

以消除或者降低结构几何应力。

Abstract

Directing against the problem of leakage due to cracking frequently occured on welded seams between tubes of medium - or high - temperature reheater and comb - shaped sealing plates in DG1025/18. 2-Ⅱ （3） type boiler

macro - analysis and micro - analysis have been carried out for the sealing structure and the crack fracture. It is considered that the cause of failure to be creep rupture under the effect of structural geometric stress

and the type of rupture to be wedge - shaped creep rupture. For this reason

a mode of changing the welded structure between the comb - shaped sealing plates and the tubes can be used to eliminate or reduce the structural geometric stress.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of oxygenated treatment on oxide scale exfloliation

Optimization and reconstruction of superheater and reheater for a 1 000 MW tower type boiler with double-reheat cycle

Practice and optimization of combined pipe-blowing method for domestic first double-reheat unit

Arrangement optimization for temperature measuring points on tube wall of (ultra) supercritical boilers

Experimental study on optimization and adjustment of wall temperature of reheater tubes in an ultra supercritical double-reheat boiler

Related Author

CAO Jieyu

JIA Jianmin

LIU Feng

TANG Liying

LIU Chao

LIU Hui

WANG Lin

GAO Jinghui

Related Institution

Xi’an Thermal Power Research Institute Co., Ltd.

Shenhua Guohua Electric Power Research Institute Company Limitied

Xi’an Thermal Power Research Institute Co., Ltd., Suzhou Branch

Huaneng Anyuan Power Generation Co., Ltd.

Huaizhe Power Fengtai Branch Co.,Ltd.

AI问答

⁰