STRENGTH ANALYSIS OF CRACKED PART ON CYLINDER WALL IN STEAM TURBINE

doi:10.19666/j.rlfd.2003.09.007

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

STRENGTH ANALYSIS OF CRACKED PART ON CYLINDER WALL IN STEAM TURBINE

更新时间：2025-09-28

- STRENGTH ANALYSIS OF CRACKED PART ON CYLINDER WALL IN STEAM TURBINE
- Thermal Power Generation Issue 9, Pages: 25-28(2003)
- 作者机构：
  
  1. 沙角C发电厂
  2. 国电热工研究院,广东,东莞,523908
  3. ,陕西,西安,710032
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2003.09.007
  CLC： TK263
- Published：2003
- 稿件说明：
移动端阅览
STRENGTH ANALYSIS OF CRACKED PART ON CYLINDER WALL IN STEAM TURBINE[J]. Thermal power generation, 2003, (9): 25-28.
DOI：

STRENGTH ANALYSIS OF CRACKED PART ON CYLINDER WALL IN STEAM TURBINE[J]. Thermal power generation, 2003, (9): 25-28. DOI： 10.19666/j.rlfd.2003.09.007.

摘要

运用壳体理论对 5 15 0 1型汽轮机汽缸壁开裂处的内压应力和热应力进行分析计算

并对裂纹的安全性进行了评定

根据计算结果对汽缸缺陷和汽机运行提出了建议。分析认为

该汽缸裂纹是安全的

不会发生一次性脆断。但该裂纹的应力强度因子k1值已接近断裂判据值

故消除缺陷可提高汽缸运行的安全性

Abstract

Applying shell theory

the internal pressure stress and the thermal stress of the cracked part on cylinder wall in a 51-50-1 type steam turbine have been analysed and calculated

and the safety of cracks being evaluated. At the same time

some recommendations for the cylinder defects and the steam turbine operation have been suggested. It is considered from analysis that the said cracks are safe

that is to say a single-stage brittle fracture can not occur.

关键词

Keywords

references

Views

107

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

TEMPERATURE FIELD AND THERMAL STRESS FINITE ELEMENT ANALYSIS OF A 50MW STEAM TURBINE'S CYLINDER IN A POWER PLANT

CAUSE ANALYSIS OF CRACKS OCCURRED IN ANGLE-WELDING SEAM ON INLET HEADER OF LOW-TEMPERATURE SUPERHEATER

Crack detection and structure optimization for fillet welds in nozzle stubs of deaerator spray pipes

Operating state and fatigue life evaluation of boiler steam drum for domestic first set of 9F gas turbine units

THERMAL STRESS RECTIFICATION OF STEAM CYLINDER DEFORMATION

Related Author

李益民

李中华

王华

陈强

陈聪智

HU Xin-fang1

YUE Zeng-wu1

YU Guang-qiang2

Related Institution

Shanghai Jiao Tong University

Baoji Power Plant Xi'an

Shandong Electric Power Research Institute

Huaneng Dezhou Power Plant

Xi’an Thermal Power Research Institute Co., Ltd.

AI问答

⁰