Silicone rubber (SiR) composite material is a modern-day insulator for high voltage outdoor applications. The imperfection attributed to SiR is its weak resistance to tracking and erosion when exposed to an outdoor polluted environment which reduces its operational lifetime. This paper investigates the performance of SiR with the addition of 0

1

2.5

5

10 and 20% by weight contents of nano alumina (Al<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3). Inclined plane tests are performed according to IEC 60587 using the step up tracking voltage method with an initial voltage of 3.0 kV and the contaminant solution flow rate is maintained at 0.3 ml/min using a peristaltic pump. The applied voltage level is increased at a rate of 0.25 kV/h. Results suggest that physical tracking

erosion

RMS leakage current and surface partial discharge (PD) performance of samples is improved with the addition of nano alumina. The tracking length

eroded mass

RMS leakage current and average PD magnitude are measured 22%

79%

30% and 52% lesser in 20 wt% relative to 0 wt%

respectively. A thermal distribution analysis is undertaken with infrared camera and it is discovered that heat is accumulated in the discharge area of the liquid flow. The maximum temperature on the insulating specimen is decreased with increasing nanofiller contents. The above promising findings can be due to better thermal stability with low chain mobility at the interaction zone of SiR and alumina. Moreover

less liquid evaporation due to better thermal conduction and improved physical bonding between SiR and nano alumina are possible reasons behind the excellent performance of nanocomposites.