Experimental study on the effect of sulfate on glutenite weathering in 
Maijishan grottoes

WANG Feng-rui; JIAO Da-ding; LIU Ping; SUN Bo; WANG Jia-jie; YANG Hong-rui

doi:10.16285/j.rsm.2019.1508

English Version Journal Login

您当前的位置：

首页 >

文章列表页 >

Experimental study on the effect of sulfate on glutenite weathering in Maijishan grottoes

更新时间：2026-06-25

- Experimental study on the effect of sulfate on glutenite weathering in Maijishan grottoes
- Vol. 41, Issue 7, Pages: 2199-2206(2020)
- 作者机构：
  
  1. 兰州大学土木工程与力学学院,甘肃,兰州,730000
  2. 中铁西北科学研究院有限公司,甘肃,兰州,730000
  3. 兰州大学西部灾害与环境力学教育部重点实验室,甘肃,兰州,730000
- 作者简介：
- 基金信息：
- DOI：10.16285/j.rsm.2019.1508
  CLC： TU452
- Online First：10 September 2020，
  
  Published：2020
- 稿件说明：
移动端阅览
WANG Feng-rui, JIAO Da-ding, LIU Ping, et al. Experimental study on the effect of sulfate on glutenite weathering in Maijishan grottoes[J]. 2020, 41(7): 2199-2206.
DOI：

WANG Feng-rui, JIAO Da-ding, LIU Ping, et al. Experimental study on the effect of sulfate on glutenite weathering in Maijishan grottoes[J]. 2020, 41(7): 2199-2206. DOI： 10.16285/j.rsm.2019.1508.

摘要

麦积山石窟砂砾岩在盐分参与下出现粉化、剥落等现象，这大大加速了石窟岩体的风化进程。通过对砂砾岩进行毛细迁移及循环劣化试验，研究了硫酸盐在砂砾岩中的运移规律，分析了盐分参与下砂砾岩的破坏特征，并得出了其产生的结晶压力。结果表明：硫酸钠结晶使砂砾岩发生显著破坏；硫酸盐在砂砾岩中的运移呈现一定的规律性；硫酸钠溶液的浓度达到0.95～1.13 mol/L区间时，砂砾岩开始破坏，并且得出试验条件下结晶压力理论最大值可以达到33 MPa。

Abstract

The phenomenon of silting and spalling is very common during glutenite weathering in Maijishan grottoes. Previous studies have shown that the participation of salt greatly accelerates the weathering process of rock. In this paper

several sets of cylindrical specimens made of glutenite were used in two tests

namely capillary migration test and cycle degradation test. The migration patterns of sulfate in samples and the failure characteristics of the glutenite specimens were discussed. Based on the experimental data and theoretical analysis

the crystallization pressure in glutenite samples was calculated. This is an important parameter for judging the damage of glutenite caused by salt crystallization. The results show that: the crystallization of sodium sulfate caused substantial damage to glutenite; the migration of sulfate in glutenite had regularity; when the concentration of sodium sulfate solution was between 0.95 mol/L and 1.13 mol/L

the destruction of the conglomerate began. The theoretical maximum crystallization pressure could reach 33 MPa under the experimental conditions.

关键词

Keywords

references

Views

156

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Progressive fracture evolution and mechanical response of cavity-containing sandstone under low-frequency disturbance

Evaluation of liquefaction flow characteristics and soil state of saturated sand based on tension and compression apparent viscosity

Optimal design of lining structure in artificial cavern of compressed air energy storage

Physical-mechanical properties and durability analysis of foamed lightweight soil based on excavated soil and fly ash

Mechanical properties and microstructural evolution of peaty soils subjected to freeze-thaw cycles

Related Author

No data

Related Institution

No data

AI问答

⁰