Experiments on static characteristics of sea sand solidified 
by polyurethane

GAO Yun-chang; GAO Meng; YIN Shi

doi:10.16285/j.rsm.2019.0202

English Version Journal Login

您当前的位置：

首页 >

文章列表页 >

Experiments on static characteristics of sea sand solidified by polyurethane

更新时间：2026-06-25

- Experiments on static characteristics of sea sand solidified by polyurethane
- Vol. 40, Issue S1, Pages: 231-236(2019)
- 作者机构：
  
  1. 山东科技大学山东省土木工程防灾减灾重点实验室,山东,青岛,266590
  2. 山东科技大学土木工程与建筑学院,山东,青岛,266590
- 作者简介：
- 基金信息：
- DOI：10.16285/j.rsm.2019.0202
  CLC： TU443
- Online First：16 August 2019，
  
  Published：2019
- 稿件说明：
移动端阅览
GAO Yun-chang, GAO Meng, YIN Shi. Experiments on static characteristics of sea sand solidified by polyurethane[J]. 2019, 40(S1): 231-236.
DOI：

GAO Yun-chang, GAO Meng, YIN Shi. Experiments on static characteristics of sea sand solidified by polyurethane[J]. 2019, 40(S1): 231-236. DOI： 10.16285/j.rsm.2019.0202.

摘要

聚氨酯是一种高聚物，可以通过填充孔隙、胶结土颗粒的作用达到提高强度和整体性的目的。采用聚氨酯对海砂进行固化处理，设计无侧限抗压强度试验和三轴剪切试验，分析不同胶凝时间和不同固化剂含量下固化海砂的强度特性和变形特性。试验结果表明，随着胶凝时间的增加，固化海砂的强度提高，在固化时间3 h时就可达到稳定强度的80%以上，并且在试验所采取的质量比范围内，质量比越高，固化效果越好；聚氨酯泡沫填充到孔隙中使颗粒之间的咬合力增大，增强了黏聚力；颗粒重排列的阻力增大，使得海砂抵抗变形的能力增加，峰值强度提高，静力特性发生明显变化。

Abstract

Polyurethane is a kind of polymer

which can be used to improve the strength and integrity of material by filling pore and cementing soil particles. This paper used polyurethane to solidify the sea sand. The unconfined compressive strength tests and triaxial shear tests were designed to analyze the strength and deformation characteristics of solidified sea sand under different gelation time and different contents of curing agent. The experimental results show that with the increase of cementing time

the strength of solidified sea sand increases. More than 80% of the stable strength can be achieved at the solidification time of 3 hours. Moreover

the higher the mass ratio

the better the solidification effect. The polyurethane foam is filled into the pores

which increases the bite force between particles and enhances cohesion. The resistance of particle rearrangement increases

making the ability of sea sand to resist deformation become stronger

increasing the peak strength and changing the static properties.

关键词

Keywords

references

Views

174

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Law study of dynamic discharge water of marine soft clay under impact loading

Dilatancy of coarse-grained soil in large-scale triaxial tests study

CT triaxial rheological test on coarse-grained soils

Analysis of slope stability based on modified relationship of intermediate principal stress

Experimental investigation of hydraulic conductivity of sand under high confining pressure

Related Author

LIU Yong-jian

FU Na

LIN Hui

JIANG Jing-shan

CHENG Zhan-lin

ZUO Yong-zhen

DING Hong-shun

JIANG Jing-shan

Related Institution

Institute of Geotechnical Engineering, Guangdong University of Technology

School of Civil Engineering, Nanjing Institute of Technology

Key Laboratory of Geotechnical Mechanics and Engineering of Ministry of Water Resources, Yangtze River Scientific Research Institute

Department of Civil Engineering, Beihang University

State Key Laboratory of Structural Analysis for Industrial Equipment, Dalian University of Technology

AI问答

⁰