Cause Analysis of Cast Aluminum Tail Tube Fracture and Detachment in Cable Terminal

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Installation, Operation & Maintenance | 更新时间：2025-12-18

- Cause Analysis of Cast Aluminum Tail Tube Fracture and Detachment in Cable Terminal
- “Experts analyzed the cause of the fracture and detachment of the cast aluminum tail pipe at a 110 kV cable terminal and found that porosity defects and material composition segregation were key factors, providing reference for solving similar faults.”
- Wire & Cable Vol. 68, Issue 11, Pages: 61-66(2025)
- 作者机构：
  
  1.浙江省电力锅炉压力容器检验所有限公司，杭州 310014
  2.国网宁波供电公司，宁波 315016
  3.国网绍兴供电公司，绍兴 312000
- 作者简介：
- 基金信息：
- DOI：10.16105/j.dxdl.1672-6901.20250096
  CLC： [TM564
- Received：27 April 2025，
  
  Revised：2025-06-12，
  
  Accepted：30 July 2025，
  
  Published：25 November 2025
- 稿件说明：
移动端阅览
龚金龙, 鲁旷达, 孙庆峰, 等. 一起电缆终端铸铝尾管断裂脱落原因分析[J]. 电线电缆, 2025, 68(11): 61-66

GONG J L, LU K D, SUN Q F, et al. Cause analysis of cast aluminum tail tube fracture and detachment in cable terminal[J]. Wire & Cable, 2025, 68(11): 61-66
龚金龙, 鲁旷达, 孙庆峰, 等. 一起电缆终端铸铝尾管断裂脱落原因分析[J]. 电线电缆, 2025, 68(11): 61-66 DOI： 10.16105/j.dxdl.1672-6901.20250096.

GONG J L, LU K D, SUN Q F, et al. Cause analysis of cast aluminum tail tube fracture and detachment in cable terminal[J]. Wire & Cable, 2025, 68(11): 61-66 DOI： 10.16105/j.dxdl.1672-6901.20250096.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

AI导读

AI脑图

AI问答

⁰