Composite Material Covered nZVI to Remove Cr（Ⅵ） in Wastewater

詹聪; 邓同辉; 李琴; 张丰; 黎建刚; 唐红梅

doi:10.16056/j.2096-7705.2021.02.021

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Composite Material Covered nZVI to Remove Cr（Ⅵ） in Wastewater

更新时间：2026-01-19

- Composite Material Covered nZVI to Remove Cr（Ⅵ） in Wastewater
- Issue 2, Pages: 110-114(2021)
- 作者机构：
  
  1. 江西省科学院能源研究所
  2. 丽水市生态环境局
- 作者简介：
- 基金信息：
- DOI：10.16056/j.2096-7705.2021.02.021
  CLC： X703;TB33
- Published：2021
- 稿件说明：
移动端阅览
詹聪, 邓同辉, 李琴, et al. Composite Material Covered nZVI to Remove Cr（Ⅵ） in Wastewater[J]. 2021, (2): 110-114.
DOI：

詹聪, 邓同辉, 李琴, et al. Composite Material Covered nZVI to Remove Cr（Ⅵ） in Wastewater[J]. 2021, (2): 110-114. DOI： 10.16056/j.2096-7705.2021.02.021.

摘要

采用微乳液法合成纳米零价铁（nZVI）颗粒。以壳聚糖、聚丙烯酸-苯乙烯（PAA-b-PS）为外壳采用离位法制备了壳聚糖/PAA-b-PS双包埋纳米零价铁颗粒（CS-PAA-b-PS-Fe）;运用TEM、XRD对CS-PAA-b-PS-Fe材料进行表征

并用于水中Cr（Ⅵ）的去除。表征结果显示C-PAA-b-PS-Fe具有核壳结构

能有效地防止纳米零价铁的团聚。实验结果表明:CS-PAA-b-PS-Fe还原Cr（Ⅵ）的最佳质量浓度比为0.2∶1∶1;温度为25℃

Cr（Ⅵ）初始浓度C

=100 mg/L下

投入0.1 g/L的CS-PAA-b-PS-Fe材料

反应100 min达到平衡

其Cr（Ⅵ）最大去除率达到100%。在酸性环境下

C-PAA-b-PS-Fe去除Cr（Ⅵ）主要以吸附和还原反应为主。

Abstract

Nano-zero-valent iron（nZVI） particles were synthesized by microemulsion method. Chitosan and polyacrylic acidstyrene（PAA-b-PS） as the shell were used prepare the chitosan/PAA-b-PS double-embedded nano-zero iron particles（CSPAA-b-PS-Fe） by the off-site method; CS-PAA-b-PS-Fe material characterized by TEM and XRD

and be used to remove Cr（Ⅵ） in water. Characterization results show that CS-PAA-b-PS-Fe has a core-shell structure

which can effectively prevent the agglomeration of nZVI. The experimental results show that: the optimal mass concentration ratio of CS-PAA-b-PS-Fe for reducing Cr（Ⅵ） is 0.2∶1∶1; Under the conditions of Cr（Ⅵ） mass concentration 100 mg/L

CS-PAA-b-PS-Fe dosage 0.1 g/L and reaction time 100 min to reach equilibrium

the maximum removal rate of Cr（Ⅵ） reaches 100%.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

AI问答

⁰