Study on Crack Tip Temperature Field and Microstructure Damage for Wind Turbine Composite Blade

Linlin WANG; Changzheng CHEN; Bo ZHOU; Yumeng SUN; Shuang KANG; Jinyao DU

doi:10.12096/j.2096-4528.pgt.19007

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Study on Crack Tip Temperature Field and Microstructure Damage for Wind Turbine Composite Blade

New and Renewable Energy | 更新时间：2025-07-04

- Study on Crack Tip Temperature Field and Microstructure Damage for Wind Turbine Composite Blade
- Power Generation Technology Vol. 40, Issue 6, Pages: 605-610(2019)
- 作者机构：
  
  沈阳工业大学机械工程学院, 辽宁省沈阳市 110870
- 作者简介：
- 基金信息：
  
  National Natural Science Foundation of China(51575361);National Natural Science Foundation of China(51675350)
- DOI：10.12096/j.2096-4528.pgt.19007
  CLC：
- Received：21 January 2019，
  
  Published：31 December 2019
- 稿件说明：
移动端阅览
Linlin WANG, Changzheng CHEN, Bo ZHOU, et al. Study on Crack Tip Temperature Field and Microstructure Damage for Wind Turbine Composite Blade[J]. Power Generation Technology, 2019, 40(6): 605-610.
DOI：

Linlin WANG, Changzheng CHEN, Bo ZHOU, et al. Study on Crack Tip Temperature Field and Microstructure Damage for Wind Turbine Composite Blade[J]. Power Generation Technology, 2019, 40(6): 605-610. DOI： 10.12096/j.2096-4528.pgt.19007.

摘要

依据热力耦合建立含微缺陷叶片的裂尖温度场数值模型，并研究了微缺陷叶片断裂微观损伤方式。首先，建立裂尖温度场数学模型需要确定塑性区范围和塑性区内的内热流密度函数。基于正交各向异性复合材料裂纹尖端应力场和Tsai-Wu屈服准则理论推导，得到含微缺陷风电叶片Ⅰ/Ⅱ复合型裂纹的塑性区范围；内热流密度函数按照裂纹扩散规律构造。其次，利用电子扫描电镜技术对叶片试件的断口失效微观结构进行检测。通过红外热像仪监测微缺陷叶片试件表面温度实验，验证了裂尖温度场计算模型的准确性；确定计算温度场模型中内热流密度函数幂数为2；通过显微技术发现含气泡缺陷的叶片试件有纤维断裂、基体开裂损伤方式。

Abstract

The crack tip temperature field of blade with micro-defect based on the thermo-mechanical was studied. The microstructure damage mode of specimen fracture was proposed. The numerical model of the crack tip temperature field was established by the plastic zone and the internal heat flux density function. The plastic zone boundary model of Ⅰ/Ⅱ crack propagation with micro-defects wind turbine blade was deduced by crack tip stress of orthotropic composite and Tsai-Wu failure criterion. The heat flux density function of crack tip temperature field was constructed by crack propagation law. The fracture failure microstructure of the blade specimen was examined by scanning electron microscopy(SEM). The surface temperature of wind blade specimen with micro-defect by infrared thermography was monitored. The surface temperature of specimen was consistent with numerica l result of crack tip temperature field. The power of heat flux density function is 2. It was found that the damage modes of blade specimen with bubble defects were fiber fracture

matrix cracking.

关键词

Keywords

references

胡燕平, 戴巨川, 刘德顺.大型风力机叶片研究现状与发展趋势[J].机械工程学报, 2013, 49(20):140-151.

陶维翔.叶尖小翼对风力机气动性能的影响分析[J].分布式能源, 2019, 4(2):47-52.

孟梨雨, 曾智, 王冠, 等.风电叶片蒙皮与腹板粘接红外热像检测研究[J].光电子技术, 2015, 35(3):174-178.

Shokrieh M M, Rafiee R.Simulation of fatigue failure in a full composite wind turbine blade[J].Composite Structures, 2006, 74(3):332-342.

周伟, 孙诗茹, 冯艳娜, 等.风电叶片复合材料拉伸损伤破坏声发射行为[J].复合材料学报, 2013, 30(2):240-246.

郭杏林, 王晓钢.疲劳热像法研究综述[J].力学进展, 2009, 39(2):217-227.

Ranc N, Palin-luc T, Paris P C, et al.About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading[J]. International Journal of Fatigue, 2014, 58:56-65.

Wymore M L, Dam J E V, Ceylan H, et al.A survey of health monitoring systems for wind turbines[J]. Renewable and Sustainable Energy Reviews, 2015, 52:976-990.

Palumbo D, Finis R D, Demelio P G, et al. A new rapid thermographic method to assess the fatigue limit in GFRP composites[J].Composites Part B, 2016, 103:60-67.

Liakat M, Khonsari M M.Analysis and life prediction of a composite laminate under cyclic loading[J].Composites Part B, 2016, 84:98-108.

Naderi M, Kahirdeh A, Khonsari M M.Dissipated thermal energy and damage evolution of Glass/Epoxy using infrared thermography and acoustic emission[J].Composites Part B, 2012, 43(3):1613-1620.

樊俊铃, 郭杏林.弹塑性疲劳裂纹扩展行为的数值模拟[J].机械工程学报, 2015, 51(10):33-40.

姚磊江, 童小燕, 吕胜利.关于疲劳能量理论若干问题的讨论[J].机械强度, 2004, 26(S):278-281.

周勃, 俞方艾, 张亚楠, 等.风力机叶片原生缺陷转捩的能量释放机理研究[J].仪器仪表学报, 2017, 38(12):3053-3060.

Bhalla K S, Zehnder A T, Han X.Thermomechanics of slow stable crack growth:closing the loop between computational modeling[J]. Engineering Fracture Mechanics, 2003, 70(17):2439-2458.

沈观林.复合材料力学[M].北京:清华大学出版社, 2013:174-185.

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

AI问答

⁰