Analysis and Treatment on Casting Three-way Crack of High Temperature Header in 600MW Thermal Power Unit

CHEN Shunqing; YU Changjiang; MAO Zhizhong; TANG Haifeng

English Version Journal Login

您当前的位置：

首页 >

文章列表页 >

Analysis and Treatment on Casting Three-way Crack of High Temperature Header in 600MW Thermal Power Unit

更新时间：2025-04-27

- Analysis and Treatment on Casting Three-way Crack of High Temperature Header in 600MW Thermal Power Unit
- Vol. 40, Issue 1, Pages: 53-56(2021)
- 作者机构：
  
  河北国华沧东发电有限责任公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TM621;TG441.7
- Published：2021
- 稿件说明：
移动端阅览
[1]陈顺青,于长江,毛志忠,唐海峰.600MW机组高温集箱铸造三通焊缝裂纹分析及处理[J].河北电力技术,2021,40(01):53-56.

CHEN Shunqing, YU Changjiang, MAO Zhizhong, et al. Analysis and Treatment on Casting Three-way Crack of High Temperature Header in 600MW Thermal Power Unit[J]. 2021, 40(1): 53-56.
[1]陈顺青,于长江,毛志忠,唐海峰.600MW机组高温集箱铸造三通焊缝裂纹分析及处理[J].河北电力技术,2021,40(01):53-56. DOI：

CHEN Shunqing, YU Changjiang, MAO Zhizhong, et al. Analysis and Treatment on Casting Three-way Crack of High Temperature Header in 600MW Thermal Power Unit[J]. 2021, 40(1): 53-56. DOI：

摘要

针对某火电厂600MW亚临界机组高温集箱铸造三通焊缝熔合线出现表面环向裂纹的问题

从宏观应力、材料特性及化学成分等方面分析裂纹产生的原因

认为裂纹属再热裂纹

由焊缝熔合线处复杂应力释放造成。给出采用合理的焊接及热处理工艺修复上述裂纹缺陷的处理措施

并提出对该类三通焊缝的技术监督及处理建议。

Abstract

According to the problem of casting three-way weld fusion line circular crack of high temperature header in 600 MW subcritical unit

this paper analyzes the reasons from the aspects of macroscopic stress

material properties and chemical composition

it is finally confirmed that the crack belongs to reheat crack

caused by the release of complex stress at the weld fusion line.In this paper

we provide a reasonable welding and heat treatment measure to repair the above crack defects and put forward related suggestions to prevent above crack defects.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Energy Saving Reform of Clean and Hydrophobic System in 660 MW Subcritical Plant

Analysis of Cracking on High and Medium Pressure Rotor of 300 MW Team Turbine

基于半不变量随机潮流的电网连锁故障预防

基于深度学习的变电站高压柜内绝缘子缺陷检测

基于混合有限时间的四旋翼无人机轨迹跟踪控制与巡检优化

Related Author

GUO Ruitao

SUN Guangjian

LI Zhigang

AN Rushan

LI Haisheng

Related Institution

Huaneng Hanfeng Power Plant

Huaneng Shang′an Power Plant

Datang Wu’an Power Generation Co.,Ltd.

AI问答

⁰