- Effect of solution treatment on microstructure and property of cold bending TP347H steel tube
- Vol. 32, Issue 6, Pages: 19-22(2012)
- 作者机构：
  
  1. 湖南省湘电锅炉压力容器检验中心有限公司
  2. 湖南省电力公司科学研究院
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG156.94
- Published：2012
- 稿件说明：
移动端阅览
[1]牟申周,谢亿,胡加瑞,彭碧草,陈红冬.固溶处理对冷弯TP347H钢管组织和性能的影响[J].湖南电力,2012,32(06):19-22.

MOU Shen-zhou1, XIE Yi2, HU Jia-rui2, et al. Effect of solution treatment on microstructure and property of cold bending TP347H steel tube[J]. 2012, 32(6): 19-22.
[1]牟申周,谢亿,胡加瑞,彭碧草,陈红冬.固溶处理对冷弯TP347H钢管组织和性能的影响[J].湖南电力,2012,32(06):19-22. DOI：

MOU Shen-zhou1, XIE Yi2, HU Jia-rui2, et al. Effect of solution treatment on microstructure and property of cold bending TP347H steel tube[J]. 2012, 32(6): 19-22. DOI：

摘要

采用金相试验、扫描电镜试验、硬度试验和双环电化学动电位再活化法（DL-EPR）试验等方法

研究不同的固溶处理温度对冷弯TP347H钢管组织和性能的影响。结果表明

TP347H钢管经过冷弯变形后

晶内有大量的滑移线出现

硬度超出标准许可范围

抗晶间腐蚀能力降低。经固溶处理后

滑移线和第二相减少

硬度降低。固溶处理温度对弯管的抗晶间腐蚀能力影响很大

从1050℃到1150℃

弯管的抗晶间腐蚀能力先变强

在1 100℃达到峰值

然后变弱。TP347H的最佳固溶处理温度为1 100℃。

Abstract

Effect of different solution treatment temperature on microstructure and property of cold bending TP347H steel tube is studied by microscopic test

scanning electron microscopy test

hardness test

DL-EPR test and other methods.The results show that there are a lot of slip lines in the intragranular of TP347H tube after cold bending deformation.The hardness exceeds the standard permission level and resistance to intergranular corrosion is reduced.After solution treatment

slip line and second-phase is reduced and the hardness is decreased.The influence of solution treatment temperature on the resistance to intergranular corrosion of elbow tube is significant.From 1 050 ℃ to 1 150 ℃

resistance to intergranular corrosion of elbow tube become strong first.It reach the peak at 1 100 ℃

then it becomes weak gradually.The best solution treatment temperature of TP347H steel tube is 1 100 ℃.

关键词

Keywords

references

Views

181

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Researches on TP347H/T91 dissimilar metal welding process

Study on microstructure and performance of 12Cr2Mo steel welded joint after long-term service

Dew point corrosion of air preheater and its precaution

Related Author

DENG Jin-jian

HUANG Fen

LI Wenbo

XIE Yi

LI Dengke

HU Jiarui

CHEN Hongdong

Related Institution

Hunan Thermal Power Construction Company

Sinoma Science and Technology Development Center Limited

State Grid Hunan Electric power Corporation Research Institute

AI问答

⁰