Fracture analysis for dissimilar metal welded joints of 12Cr1MoVG/TP347H in a utility boiler
更新时间：2025-09-28

    • Fracture analysis for dissimilar metal welded joints of 12Cr1MoVG/TP347H in a utility boiler

    • Thermal Power Generation   Issue 4, (2017)
    • CLC： TK442

    • Published Online：26 April 2017，

      Published：2017

    移动端阅览

  • ZHANG Zonglai. Fracture analysis for dissimilar metal welded joints of 12Cr1MoVG/TP347H in a utility boiler[J]. Thermal power generation, 2017, (4). DOI：

  •  
  •  

0

Views

984

下载量

0

CSCD

Alert me when the article has been cited
提交
Tools
Download
Export Citation
Share
Add to favorites
Add to my album

Related Articles

Fracture failure analysis of Ni-based bolts for ultra-supercritical units
CAUSE ANALYSIS OF WELDED JOINT CRACKING FOR G102 STEEL HIGHTEMPERATURE TUBE
Reason analysis for fracture occurred in axial induced draft fan blade of a 600 MW unit
Thermal fatigue failure analysis for drainage-tank in hot section of reheat pipeline in an ultra supercritical 1 000 MW unit
Development and numerical simulation for a high efficiency steam soot blower

Related Author

JIANG Tao
WANG Jianguang
ZHANG Zhibo
MAI Yongqiang
GAO Jing
CAI Heping
JIANG Feng
YU Song

Related Institution

Military Grain City Power Plant
Junliangcheng Power Plant Tianjin
Xi’an TPRI Energy Conservation Technology Co., Ltd.
Xi’an Thermal Power Research Institute Co., Ltd.
0