STUDY ON MICROSTRUCTURE AND PERFORMANCE OF WELDED JOINT BETWEEN DIFFERENT STEELS

LI Zhenggang1; LI Yiwen2; ZHOU Jinping3 1.College of Power and Mechanical Engineering

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

STUDY ON MICROSTRUCTURE AND PERFORMANCE OF WELDED JOINT BETWEEN DIFFERENT STEELS

更新时间：2025-09-28

- STUDY ON MICROSTRUCTURE AND PERFORMANCE OF WELDED JOINT BETWEEN DIFFERENT STEELS
- Thermal Power Generation Vol. 39, Issue 5, Pages: 62-65(2010)
- 作者机构：
  
  1. 武汉大学动力与机械学院材料系
  2. 中广核工程有限公司
  3. 国电长源汉川第一发电有限公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG407;TM621
- Published：2010
- 稿件说明：
移动端阅览
LI Zhenggang1, LI Yiwen2, ZHOU Jinping3 1.College of Power and Mechanical Engineering. STUDY ON MICROSTRUCTURE AND PERFORMANCE OF WELDED JOINT BETWEEN DIFFERENT STEELS[J]. Thermal power generation, 2010, 39(5): 62-65.
DOI：

LI Zhenggang1, LI Yiwen2, ZHOU Jinping3 1.College of Power and Mechanical Engineering. STUDY ON MICROSTRUCTURE AND PERFORMANCE OF WELDED JOINT BETWEEN DIFFERENT STEELS[J]. Thermal power generation, 2010, 39(5): 62-65. DOI：

摘要

对长期运行后的TP347H与钢102异种钢焊接接头进行了组织与性能试验研究

对其组织老化与性能变化进行了分析。结果表明

长期运行后钢102金相组织达到4级球化

TP347H钢有沿晶碳化物析出

钢102侧熔合线处存在一个过渡层

该处析出较多碳化物

硬度较高

母材中的碳向焊缝迁移。

Abstract

A test study on microstructure and performance of welded joint between different steels;i.e.TP347H steel and 102 steel

after long-term service has been carried out

the aging of microstructure and variation of performance being analysed.Results show that the metallographic structure of 102 steel after long-term service has reached 4-grade spheroidization

and the carbide precipitation appears along the grain boundary in TP347H steel;on the fusion line at the 102 steel side

there is a transitional layer

in which precipitation of more carbide appears

and has higher hardness

the carbon existing in base metal removes to the welded joint.

关键词

Keywords

references

Views

159

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

THE CARBIDE CONTAINED IN HCM25(T23) STEEL AND EVOLUTION REGULARITY THEREOF

CORROSION CHARACTERS OF TP347H STEEL UNDER ATMOSPHERE OF SUPERHEATERS OF BIOMASSBURNED BOILERS(Ⅱ)

CORROSIVE CHARACTORS OF TP347H STEEL IN SUPERHEATER'S ATMOSPHERE OF BIOMASS-BURNED BOILER

CAUSE ANALYSIS OF DESUPERHEATER FRACTURE FOR BOILER OF 600 MW UNIT

CAUSE ANALYSIS OF WELDED SEAM CRACKING OCCURRED ON TUBES OF T91/TP34H HIGH-TEMPERATURE REHEATER

Related Author

ZHANG Hongjun1 1.Xi'an Thermal Power Research Institute Co.Ltd.

TANG Liying1

ZHOU Rongcan1

HOU Shufang1

NIE Ming2

YU Zaisong1

WU Zhan-song21.Guangdong Electric Power Design Institute

YIN Jia-min1

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Guangdong Power Grid Corporation Electric Power Science Research Institute

Guangdong Electric Power Design and Research Institute

Key Laboratory of Thermal Science and Power Engineering, Ministry of Education, Tsinghua University

Datang Panshan Power Generation Co., Ltd

AI问答

⁰