ANALYSIS OF CLAMPING TUBE LEAKAGE FOR REAR PLATEN SUPERHEATER OF THE BOILER

LI Xichao; ZHANG Lifeng; DUAN JiangShaanxi Electric Power Science Research Institute

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

ANALYSIS OF CLAMPING TUBE LEAKAGE FOR REAR PLATEN SUPERHEATER OF THE BOILER

更新时间：2025-09-28

- ANALYSIS OF CLAMPING TUBE LEAKAGE FOR REAR PLATEN SUPERHEATER OF THE BOILER
- Thermal Power Generation Vol. 39, Issue 10, Pages: 104-107(2010)
- 作者机构：
  
  陕西电力科学研究院
- 作者简介：
- 基金信息：
- DOI：
  CLC： TK223.32
- Published：2010
- 稿件说明：
移动端阅览
LI Xichao, ZHANG Lifeng, DUAN JiangShaanxi Electric Power Science Research Institute. ANALYSIS OF CLAMPING TUBE LEAKAGE FOR REAR PLATEN SUPERHEATER OF THE BOILER[J]. Thermal power generation, 2010, 39(10): 104-107.
DOI：

LI Xichao, ZHANG Lifeng, DUAN JiangShaanxi Electric Power Science Research Institute. ANALYSIS OF CLAMPING TUBE LEAKAGE FOR REAR PLATEN SUPERHEATER OF THE BOILER[J]. Thermal power generation, 2010, 39(10): 104-107. DOI：

摘要

对某电厂2045t/h锅炉后屏过热器泄漏的夹持管进行了宏观检验、裂纹分析、化学成分分析、拉伸性能试验、显微硬度试验、金相组织分析、晶间腐蚀试验等。结果表明

后屏过热器夹持管泄漏的原因为蒸汽侧晶间腐蚀开裂。首先在夹持管弯头中性面的内壁处产生晶间腐蚀裂纹

随后沿管壁厚度方向沿晶扩展

直至穿透泄漏。

Abstract

The causes of clamping tube leakage for rear platen superheater of a 2 045 t/h boiler in one power plant have been analysed by using methods of macroscopic inspection

crack analysis

chemical elements analysis

tensile strength analysis

microscopic hardness test

metallographic structure analysis

intergranular corrosion test

etc..The results show that the clamping tube leakage of rear platen superheater is caused by intergranular corrosion cracking on the steam side.Firstly the intergranular corrosion cracks happened at inner wall of middle profile in elow of the clamping tube

and then extended along grain in direction of the tube wall thickness untill penetration leakage.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

TEST AND STUDY ON OVERTEMPERATURE TUBEBURST OF HEATING SURFACE FOR 670t/h BOILER IN ZHANGZE POWER PLANT

CAUSE ANALYSIS AND PREVENTION OF ROOF TYPE SUPERHEATER LEAKAGE FOR BOILERS

ANALYSIS OF AND STUDY ON RETROFIT AND APPLICATION RESULT OF ECONOMIZER IN THERMAL POWER PLANT

CAUSE ANALYSIS OF CRACKS OCCURRED IN ANGLE-WELDING SEAM ON INLET HEADER OF LOW-TEMPERATURE SUPERHEATER

ANALYSIS OF CRACKS IN WELD JOINT OF T91 STEEL IN HIGH-TEMPERATURE REHEATER

Related Author

蔡新春

史晓华

郝宏生

王志军

李王斌

郭起旺

李兵

史联青

Related Institution

Shanxi Electric Power Research Institute

Zhangze Power Plant

Central South University

AI问答

⁰