INFLUENCE OF ADDING OXYGEN INTO FEED-WATER TREATMENT UPON HIGH-TEMPERATURE OXIDE SKIN FORMED IN THE SUPERHEATOR

ZHANG Guangwen1; SUN Benda2; ZHANG Jinsheng1; GU Qinghua3; CAI Jingguang1 1.Shenhua Guohua(Beijing) Electric Power Research Institute

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

INFLUENCE OF ADDING OXYGEN INTO FEED-WATER TREATMENT UPON HIGH-TEMPERATURE OXIDE SKIN FORMED IN THE SUPERHEATOR

更新时间：2025-09-28

- INFLUENCE OF ADDING OXYGEN INTO FEED-WATER TREATMENT UPON HIGH-TEMPERATURE OXIDE SKIN FORMED IN THE SUPERHEATOR
- Thermal Power Generation Vol. 41, Issue 1, Pages: 31-33(2012)
- 作者机构：
  
  1. 神华国华(北京)电力研究院
  2. 西安热工研究院有限公司
  3. 国华太仓发电有限责任公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TM621.8
- Published：2012
- 稿件说明：
移动端阅览
ZHANG Guangwen1, SUN Benda2, ZHANG Jinsheng1, et al. INFLUENCE OF ADDING OXYGEN INTO FEED-WATER TREATMENT UPON HIGH-TEMPERATURE OXIDE SKIN FORMED IN THE SUPERHEATOR[J]. Thermal power generation, 2012, 41(1): 31-33.
DOI：

ZHANG Guangwen1, SUN Benda2, ZHANG Jinsheng1, et al. INFLUENCE OF ADDING OXYGEN INTO FEED-WATER TREATMENT UPON HIGH-TEMPERATURE OXIDE SKIN FORMED IN THE SUPERHEATOR[J]. Thermal power generation, 2012, 41(1): 31-33. DOI：

摘要

以某超临界660MW机组为例进行了给水加氧处理试验

测量比对加氧前后过热器氧化皮的生长速率

并对氧化皮结构、成分的变化进行分析。结果表明

给水加氧处理并未加快T23和T91材质过热器氧化皮的生成速度及促进其脱落

但对TP347H材质的过热器

加氧处理具有促进其氧化皮剥离的作用。因此

采用给水加氧处理的关键是控制机组起、停时的温度以抑制加氧后不锈钢氧化皮的大量脱落。

Abstract

A test of adding oxygen into feed-water treatment has been carried out on one supercritical 600 MW unti.Through measuring the growth rate of oxide skin formed in the superheater

as well as analysing the micro-structure and the variation of composition in the said oxide skin

it shows that the adding oxygen into feed-water treatment hadn't quickened the growth rate of oxide skin formed in the superheaters made from T23 and T91 steel materials

and hadn't promoted the fall-off of said oxide skin

however

in superheater made from TP347H steel

the adding oxygen into feed-water treatment boasts effect to promote the peel-off of oxide skin

where as the key of control is controlling the temperature during start-up and shutdown of unit

therefore

in the process of using the above-mentioned treatment to inhibit corrosion of the superheater

the most crucial problem is to control the fall-off of oxide skin in vast amount from stainless steel tubes after using the adding oxygen treatment.

关键词

Keywords

references

Views

404

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of oxygenated treatment on oxide scale exfloliation

Application of treatment technology for oxide scale on superheaters

Arrangement optimization for temperature measuring points on tube wall of (ultra) supercritical boilers

Simulation on wall temperature and oxide scale thickness of boiler superheaters based on discrete quasi two dimensional lumped parameter model

Experimental study on growth rate of oxide scale on superheater and reheater tubes in ultra-supercritical units

Related Author

CAO Jieyu

JIA Jianmin

LIU Feng

TANG Liying

GAN Chaoqi

LI Ying

ZHANG Junjie

DONG Kun

Related Institution

Xi’an Thermal Power Research Institute Co., Ltd.

Hebei Guohua Dingzhou Power Generation Co.,Ltd.,Dingzhou

Shenhua Guohua Electric Power Research Institute Company Limitied

School of Power and Mechanical Engineering, Wuhan University

Huaizhe Power Fengtai Branch Co.,Ltd.

AI问答

⁰