TUBE BURST OF FINAL REHEATER ON BOILER OF A 1 000 MW ULTRA SUPERCRITICAL UNIT:CAUSE ANALYSIS

QIN Chengpeng1; WANG Liang1; LI Liang1; ZHONG Shipeng2; WANG Peng1; WANG Fugui1 1.Xi'an Thermal Power Research Institute Co.Ltd.

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

TUBE BURST OF FINAL REHEATER ON BOILER OF A 1 000 MW ULTRA SUPERCRITICAL UNIT:CAUSE ANALYSIS

更新时间：2025-09-28

- TUBE BURST OF FINAL REHEATER ON BOILER OF A 1 000 MW ULTRA SUPERCRITICAL UNIT:CAUSE ANALYSIS
- Thermal Power Generation Vol. 41, Issue 10, Pages: 69-72(2012)
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 广东惠州平海发电厂有限公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TK228
- Published：2012
- 稿件说明：
移动端阅览
QIN Chengpeng1, WANG Liang1, LI Liang1, et al. TUBE BURST OF FINAL REHEATER ON BOILER OF A 1 000 MW ULTRA SUPERCRITICAL UNIT:CAUSE ANALYSIS[J]. Thermal power generation, 2012, 41(10): 69-72.
DOI：

QIN Chengpeng1, WANG Liang1, LI Liang1, et al. TUBE BURST OF FINAL REHEATER ON BOILER OF A 1 000 MW ULTRA SUPERCRITICAL UNIT:CAUSE ANALYSIS[J]. Thermal power generation, 2012, 41(10): 69-72. DOI：

摘要

对某台超超临界1 000MW机组的锅炉末级再热器HR3C爆管进行了宏观形貌观察、金相组织分析、室温拉伸性能试验、压扁试验、硬度试验、晶间腐蚀试验

并对爆口进行了扫描电镜及能谱分析。试验结果表明:末级再热器HR3C管因冷弯后未进行固溶处理

运行过程中的弯制残余应力、内压应力致使管材在有氯离子等腐蚀元素存在的环境中极易发生沿晶应力腐蚀开裂

从而导致爆管。

Abstract

Series of tests such as macroscopic morphology observation

metallographic analysis

tensile test at room temperature

flattening test

hardness test and intergranular corrosion test etc.were conducted for the burst HR3C tube.Besides

the scanning electron microscopy(SEM) with energy dispersive spectroscopy(EDS) was used to determine the corrosion product.Results show that

no solution treatment is done on the HR3C tube after its cold bending

so when it starts working

the intergranular stress corrosion cracking can easily occur in corrosive environment due to the bending residual stress and internal pressure stress.Therefore

tube burst happened.

关键词

Keywords

references

Views

165

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Fireside corrosion behavior of HR3C steel in simulated coal-fired boiler atmospheres with high sulfur concentration

ANALYSIS AND DISPOSAL OF PROBLEM FOR CARRYING BIG GRAINS INTO COAL PULVERIZING SYSTEM OF 1000 MW ULTRA-SUPERCRITICAL UNIT

STUDY ON CONSTRUCTION OF HEAT RELEASE SIGNAL FOR ULTRA-SUPERCRITICAL UNITS

SCALING ON THROTTLE PLATE OF THE WATER-WALL IN BOILER FOR ULTRA-SUPERCRITICAL UNIT AND DISPOSAL THEREOF

STUDY ON LIFE MANAGEMENT TECHNOLOGY FOR BOILERS OF ULTRA-SUPERCRITICAL 1000MW UNTIS

Related Author

LI Jiang

ZHOU Rongcan

TANG Liying

BI Kai

WANG Xin-ge

LI Hong-tao

LIANG Mao-chun Huadian Zouxian Power Plant

SUN Qun-li

Related Institution

Xi'an Thermal Power Research Institute Co.,Ltd.

Huadian Zouxian Power Plant

College of Energy and Power Engineering, North China Electric Power University

Huaneng Yuhuan Power Plant

Guangzhou Yueneng Electric Power Technology Development Co., Ltd

AI问答

⁰