Reason analysis for corrosion of low carbon steel in flue gas from an LNG power plant

CHEN Zhongbing; LU Yishi; LIU Xiao; CHEN Yuhui; ZHENG Lifeng; LEI Henghai

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Reason analysis for corrosion of low carbon steel in flue gas from an LNG power plant

更新时间：2025-09-28

- Reason analysis for corrosion of low carbon steel in flue gas from an LNG power plant
- Thermal Power Generation Vol. 43, Issue 5, Pages: 108-112(2014)
- 作者机构：
  
  1. 苏州热工研究院有限公司
  2. 深圳能源集团东部电厂
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG172.9
- Published：2014
- 稿件说明：
移动端阅览
CHEN Zhongbing, LU Yishi, LIU Xiao, et al. Reason analysis for corrosion of low carbon steel in flue gas from an LNG power plant[J]. Thermal power generation, 2014, 43(5): 108-112.
DOI：

CHEN Zhongbing, LU Yishi, LIU Xiao, et al. Reason analysis for corrosion of low carbon steel in flue gas from an LNG power plant[J]. Thermal power generation, 2014, 43(5): 108-112. DOI：

摘要

某液化天然气电站余热锅炉尾部受热面发生多次腐蚀泄漏。通过裂纹形貌观察、腐蚀产物分析、腐蚀性元素测量和管壁温度有限元计算等表明

裂纹具有典型应力腐蚀(SCC)形貌特征

腐蚀类型为沿晶SCC。导致SCC的原因是

机组调峰运行启停过程中的某些时段给水或烟气温度较低

使管外壁温度低于烟气露点从而导致烟气结露

形成SCC液态环境。SCC腐蚀的主导组分是CO2水溶液。

Abstract

Leakage occurred many times at the tail heated tubes in heat recovery steam generator(HRSG)of a power plant.Thus

much analysis were performed

such as crack morphology observation

corrosion product analysis

corrosive element measurement and tube wall temperature field FEM calculation.The results show that

the cracks have the stress corrosion cracking(SCC) characteristics and the corrosion type is intergranular fracture SCC.During a certain period of unit startup and shutdown for peaking operation

the low temperature of feed water or flue gas causes the tube outer wall temperature decreases to lower than the flue gas dew point

so the flue gas dews and the SCC solution emerges on outer wall of the tube.The CO2solution is considered as the dominant component resulting in SCC.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research on dual heat source cascade heating plan for natural gas based on heat recovery steam generator of F-class combined cycle power unit

Off-design modeling of heat recovery steam generator in heavy-duty gas turbine combined cycle unit and variable load operation research

Thermal analysis and optimization of combined cooling, heating and power system using LNG cold energy

Dynamic modeling and operating rules of three-pressure reheat waste heat recovery steam generator in heavy-duty gas turbine combined cycle unit

Related Author

WANG Yifeng

XIA Lin

ZHOU Gang

WU Changbing

XIANG Dong

ZHANG Xuehua

LIU Yin

GE Xiaoming

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Huaneng Chongqing Liangjiang Gas Turbine Power Generation Co., Ltd

School of Energy and Power Engineering, Xi'an Jiaotong University

Huaneng Nanjing Gas Turbine Power Generation Co., Ltd

Huaneng Jiangsu Energy Development Co., Ltd

AI问答

⁰