Investigation on microstucture stability of C-HRA-1 used for superheater/reheater in 700 ℃advanced ultra-supercritical unit

XU Songqian; WANG Tingting

English Version Reader LoginJournal Login

您当前的位置：

首页 >

文章列表页 >

Investigation on microstucture stability of C-HRA-1 used for superheater/reheater in 700 ℃advanced ultra-supercritical unit

更新时间：2025-09-28

- Investigation on microstucture stability of C-HRA-1 used for superheater/reheater in 700 ℃advanced ultra-supercritical unit
- Thermal Power Generation Vol. 45, Issue 6, Pages: 63-69(2016)
- 作者机构：
  
  宝山钢铁股份有限公司研究院
- 作者简介：
- 基金信息：
- DOI：
  CLC： TM621
- Published：2016
- 稿件说明：
移动端阅览
XU Songqian, WANG Tingting. Investigation on microstucture stability of C-HRA-1 used for superheater/reheater in 700 ℃advanced ultra-supercritical unit[J]. Thermal power generation, 2016, 45(6): 63-69.
DOI：

XU Songqian, WANG Tingting. Investigation on microstucture stability of C-HRA-1 used for superheater/reheater in 700 ℃advanced ultra-supercritical unit[J]. Thermal power generation, 2016, 45(6): 63-69. DOI：

摘要

研制了可工业化规模生产的700℃先进超超临界机组过/再热器用C-HRA-1镍基合金管材。采用光学显微镜、扫描电子显微镜和透射电子显微镜等分析手段

结合热力学计算

研究了C-HRA-1合金在750℃和800℃长期时效处理过程中的组织稳定性。结果表明:C-HRA-1合金管材经固溶处理后冷轧态发生完全再结晶

没有明显析出相;经800℃/12h/AC时效硬化处理后

基体上弥散分布着细小球状的γ′相

且基体中析出少量粒状MC

晶界和孪晶界析出断链状M23C6

M23C6在800℃长期时效处理中逐渐向基体溶解;750℃和800℃长期时效处理过程中

γ′相逐渐粗化并由球形趋向立方状

与时效时间相比

时效温度对γ′相粗化的影响更为显著;750℃和800℃长期时效处理过程中没有发现有害相析出

说明C-HRA-1合金管材在750℃和800℃下具有良好的组织稳定性。

Abstract

The Ni-based superalloy tube C-HRA-1is manufactured under industrial process for 700 ℃ advanced ultra-supercritical unit boiler.The microstructural evolution of C-HRA-1tube during long-term thermal exposure at 750℃and 800℃ was investigated by optical microscope

scanning electron microscope(SEM)

transmission electron microscopy(TEM)and thermal calculation.The results show that

the coldrolled tube suffered fully recrystallization after solution treatment

and no obvious precipitation was observed.After age hardening treatment at 800℃/12h/AC

γ′phase with fine spherical was dispersively distributed and small amount of MC carbide particles precipitated in the matrix.In addition

M23C6 precipitated along the grain boundaries and the twinning boundaries.During long-term thermal exposure at 750 ℃and 800 ℃

theγ′phase size increased and its spherical morphology turned to cubical with increasing exposure time and exposure temperature.However

noηphase and other new precipitate was found during long term thermal exposure.It demonstrated that the microstucture stability of the C-HRA-1tube is excellent.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

STUDY ON DIFFICULTY IN ENHANCING OXYGEN AMOUNT UNDER OPERATION AT HIGH LOAD OF FW TYPE W-SHAPED FLAME BOILER

Industrial test of dense phase conveying of pulverized coal at high pressure

Influence of time sequence parameter of Profibus on the communication stability

Characteristics and mechanism of co-slurry of lignite and petroleum coke

Effects of M/A island on microstructure and property of inter-critical heat affected zone in T24 steel welded joints

Related Author

XU Dang-qi2 (1.Yangcheng Power Generation Co Ltd

LIU Hong-gang2

YANG Zhong-can2

WEI Tong-sheng2

JIN Xin1

DUAN Bao-lin1

CHEN Zhi1

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Yangcheng International Power Generation Co., Ltd

Huaneng Clean Energy Technology Research Institute Co., Ltd

North School of Information Engineering, Xi'an University of Technology

State Key Laboratory of Clean Energy Utilization, Zhejiang University

AI问答

⁰